NiWO4 powders prepared via polymeric precursor method for application as ceramic luminescent pigments
نویسندگان
چکیده
منابع مشابه
Tubular Ceramic Foam Via Polymeric Sponge Method
Tubular ceramic foams were prepared by using natural clay as starting material and 120 ppi polyurethane foam as template via polymeric sponge method. Samples were sintered with different temperatures from 1200°C to 1280°C. The result shows that 1250°C is the ideal sintering temperature where the highest compressive strength of 1.980MPa at 47.31% porosity is obtained. The highest value in compre...
متن کاملLiNbO3 thin films prepared through polymeric precursor method
Thin films of lithium niobate were deposited on (100) silicon by the polymeric precursor method (Pechini method). Annealing in static air was performed at 500 jC for 3 h. The films obtained were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Electrical characterization of the films pointed to ferroelectricity via hysteresis loop. The diele...
متن کاملExtraction and characterization of humic acid from coal for the application as dispersant of ceramic powders
Subbituminous coal was employed as raw material for the extraction of humic acid (HA) to be applied as ceramic dispersant. The extraction process is described in detail, showing it is a relatively simple procedure, which makes the production attractive and feasible on a laboratory scale. The HA was characterized via elemental analysis, infrared spectroscopy (FTIR), thermal behavior (TGA/DTA), z...
متن کاملEthanol Electrooxidation using Ti/(RuO2)(x) Pt(1-x) Electrodes Prepared by the Polymeric Precursor Method
Este trabalho descreve um estudo detalhado da oxidação eletroquímica de etanol sobre eletrodos de Ti/(RuO2)(x)Pt(1-x) com várias composições, preparados pelo método de precursores poliméricos. Os resultados obtidos usando voltametria cíclica e cronoamperometria mostraram que a melhor composição dos eletrodos de Ti/(RuO2)(x)Pt(1-x) para os processos de oxidação do CO e do etanol é Ti/(RuO2)(0.5)...
متن کاملSynthesis and characterization of high-temperature ceramic YBCO nanostructures prepared from a novel precursor
As a new precursor, [tris(2-hydroxyacetophenato) triaqua(III)], [Y(HAP)3(H2O)3]; complex was used in thermal decomposition process for the synthesis of rod-like high-temperature ceramic YBCO with length of about 320-350 nm and diameters 60–90 nm. The as-synthesized products were characterized by XRD, FT-IR, TEM, SEM and EDX analyses. The results showed that by u...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Advanced Ceramics
سال: 2020
ISSN: 2226-4108,2227-8508
DOI: 10.1007/s40145-019-0347-z