NITRIDING PECULIARITIES OF Fe – 3 % Si TECHNICAL ALLOY
نویسندگان
چکیده
منابع مشابه
Modeling of resistance curve of high-angle grain boundary in Fe–3 wt.% Si alloy
When a propagating cleavage front encounters a high-angle grain boundary it first penetrates through the grain boundary stably. With increasing penetration depth the resistance of the grain boundary rises, resulting in the well-known R-curve. When the balance between the rates of the energy release rate and the grain boundary resistance is reached, the crack advance becomes unstable and the gra...
متن کاملHydrogen Effects on an Amorphous Fe-Si-B Alloy
HYDROGEN interaction with amorphous alloys has Ribbons (,25-mm thick) of amorphous Fe80B11Si9 were been studied extensively due to both scientific and technoused for this research. The ribbons were produced by planarlogical interest. In the framework of a more comprehensive flow casting and were kindly supplied by AlliedSignal Inc. investigation of hydrogen interaction with amorphous and (Parsi...
متن کاملSEGREGATION AT SPECIAL GRAIN BOUNDARIES IN Fe-Si ALLOY BICRYSTALS
The segre ation of silicon to the C=3, 112) and C=S, (013) symmetrical grain boundaries 1 was studied in well-fefined bicrystals of an Fe-l .9 at%Si alloy annealed in the range 773 1173 K using Auger electron spectroscopy. The segregation enthal y, AI1 = -8.1 * 0.5 kJ/mol, and entropy, AS = -69 r 0.4 i/(mol K), were determined for the (013f grain boundary in the temperature range 973 1173 K. Fo...
متن کاملTransformation Reversibility in Fe-Mn-Si Shape Memory Alloy
The change of the surface relief associated with stress-induced epsilon martensite before and after the reverse transformation in an Fe-33%Mn-6%Si alloy (Msz264K) has been investigated. The permanent strain of a 2.7% tensile-strained specimen was 1.1% after the reverse transformation. In this specimen, a large part of surface relief still remained after heating to 623K (above Af). When five tra...
متن کاملSound velocities of Fe and Fe-Si alloy in the Earth's core.
Compressional wave velocity-density (V(P)--ρ) relations of candidate Fe alloys at relevant pressure-temperature conditions of the Earth's core are critically needed to evaluate the composition, seismic signatures, and geodynamics of the planet's remotest region. Specifically, comparison between seismic V(P)--ρ profiles of the core and candidate Fe alloys provides first-order information on the ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Izvestiya Visshikh Uchebnykh Zavedenii. Chernaya Metallurgiya = Izvestiya. Ferrous Metallurgy
سال: 2015
ISSN: 2410-2091,0368-0797
DOI: 10.17073/0368-0797-2015-2-88-94