Nitriding of Nd-Fe-B and Nd-Fe-C Hard Magnetic Alloys
نویسندگان
چکیده
منابع مشابه
Effect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets
Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...
متن کاملMagnetic properties of Nd-Fe-B/α-Fe multi-layered thick film magnets
Nd-Fe-B/α-Fe multi-layered nanocomposite film-magnets were prepared from a rotating Nd2.6Fe14B/α-Fe composite target by the pulse laser deposition method with a NdYAG laser (λ=355 nm). The prepared film-magnets were composed of approximately 800 layers with the thickness of about several tens nanometre, and exhibited hard magnetic properties after annealing. The laser power for the ablation of ...
متن کاملCOERCIVITY AND THERMAL REMAGNETIZATION OF SINTERED Nd-Fe-B
Statistical methods are used to estimate coercivity J Hc and thermal remagnetization of uniaxially nucleationcontrolled permanent magnetic materials. Sintered Nd-Fe-B consists of the tetragonal magnetic Nd2FelrB phase with a volume fraction w = 80 % and of nonmagnetic phases. At temperatures above T, rz 150 K the tetragonal axis is the easy direction of magnetization [I]. It is well known [2] t...
متن کاملMAGNETIC PROPERTIES OF RAPIDLY QUENCHED (Nd, Pr)2 (Fe,Co)14B-TYPE ALLOYS
The coercivity Hc; of rapidly quenched Nd-Fe-B is linked to the multiphase structure of the alloys: high coercivities require the suppression of the &Nd solid solution and the exictence of the intergranular Nd-rich phase. In quarternary Pr-Fe-Co-B alloys H,i and the remanence J, depend in the same way on Co content as in the Nd-FeCo-B system. However, compared with rapidly quenched Nd-Co-B samp...
متن کاملSintering of Nd-Fe-B Magnets from Dy Coated Powder
High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundar...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1994
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.58.10_1220