New Ferromagnetic State Observed During Recrystallization-Process of a Cold-Rolled γ-Phase Alloy

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Grain Boundary Evolution of Cold-Rolled FePd Alloy during Recrystallization at Disordering Temperature

In this study, the grain boundary character and texture of 50% and 90% cold-rolled FePd alloy was investigated during recrystallization at 700 °C. Electron backscatter diffraction (EBSD) measurements were performed on the rolling direction to normal direction section. Kernel average misorientation (KAM) calculated from EBSD measurements was employed to determine the recrystallization fraction. ...

متن کامل

Microstructural evolution during recrystallization in hot rolled Aluminum Alloy 1050

The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...

متن کامل

Kinetics of individual grains during recrystallization of cold-rolled copper

The formation of a recrystallization texture is closely related to the nucleation and growth of recrystallizing grains, which may vary from grain to grain. Cube texture is a commonly observed recrystallization texture in face centered cubic metals of medium to high stacking fault energy after heavy cold-rolling and annealing. In this work, recrystallization of pure copper cold-rolled to a von M...

متن کامل

Kinetics of Austenite Recrystallization during the Annealing of Cold-rolled Fe-Mn-Al-C Steel

In the current study, the recrystallization behavior of 75% cold-rolled Fe-22Mn-10Al-1.4C steel during annealing at 750, 770, 790, 810, and 830°C was studied. X-ray diffraction patterns and optical microscopy were used to characterize microstructures. The Vickers Micro-hardness test was used to characterize recrystallization kinetics during annealing. Johnson-Mehl-Avrami-Kolmogorov (JMAK) model...

متن کامل

Statistical analysis on static recrystallization texture evolution in cold-rolled AZ31 magnesium alloy sheet.

Cast AZ31B-H24 magnesium alloy, comprising Mg with 3.27 wt% Al and 0.96 wt% Zn, was cold rolled and subsequently annealed. Global texture evolutions in the specimens were observed by X-ray diffractometry after the thermomechanical processing. Image-based microstructure and texture for the deformed, recrystallized, and grown grains were observed by electron backscattered diffractometry. Recrysta...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Journal of the Japan Institute of Metals and Materials

سال: 1964

ISSN: 0021-4876,1880-6880

DOI: 10.2320/jinstmet1952.28.2_108