Nanoindenter Test of 680MPa Dual Phase Steel Charged with Hydrogen
نویسندگان
چکیده
منابع مشابه
Lattice Dilation in a Hydrogen Charged Steel
The effect of hydrogen charging on the lattice dilation in an ASTM A710-HSLA steel specimen was studied using neutron diffraction. First, spatially-resolved strain measurements were made on a pre-cracked steel double cantilever beam specimen under a constant crack opening displacement (COD). Measurements were made at the crack tip region for in-plane and throughthickness lattice strains. Then, ...
متن کاملThermal Desorption Analysis of Hydrogen in Non‐hydrogen‐Charged Rolling Contact Fatigue‐Tested 100Cr6 Steel
Hydrogen diffusion during rolling contact fatigue (RCF) is considered a potential root cause or accelerator of white etching cracks (WECs) in wind turbine gearbox bearing steels. Hydrogen entry into the bearing steel during operation is thought to occur either through the contact surface itself or through cracks that breach the contact surface, in both cases by the decomposition of lubricant th...
متن کاملThermal Desorption Analysis of Hydrogen in Non-hydrogen-Charged Rolling Contact Fatigue- Tested 100Cr6 steel
Hydrogen diffusion during rolling contact fatigue (RCF) is considered a potential root cause or accelerator of white etching cracks (WECs) in wind turbine gearbox bearing steels. Hydrogen entry into the bearing steel during operation is thought to occur either through the contact surface itself, or through cracks that breach the contact surface, in both cases by the decomposition of lubricant t...
متن کاملImprovement of Mechanical Properties and Work-Hardening Behavior of Intercritically Annealed Dual Phase Steel
The effect of the initial microstructure and intercritical annealing on mechanical properties and work-hardening response of a high-formability low carbon steel were studied. The work-hardening analysis was based on the modified Crussard–Jaoul method. The ferritic-pearlitic sheets showed low strength and high total elongation with the appearance of the yield point phenomenon. The occurrence of ...
متن کاملGrain Refinement of Dual Phase Steel via Tempering of Cold-Rolled Martensite
A microstructure consisting of ultrafine grained (UFG) ferrite with average grain size of ~ 0.7 µm and dispersed nano-sized carbides was produced by cold-rolling and tempering of the martensite starting microstructure in a low carbon steel. Subsequently, fine grained dual phase (DP) steel consisting of equiaxed ferrite grains with average size of ~ 5 µm and martensite islands with average size ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Korean institute of surface engineering
سال: 2014
ISSN: 1225-8024
DOI: 10.5695/jkise.2014.47.1.033