Nanocrystalline Titania Coated Metakaolin and Rice Hull Ash Based Geopolymer Spheres for Photocatalytic Degradation of Dyes in Wastewater

Performance Evaluation and Microstructure Characterization of Metakaolin-Based Geopolymer Containing Oil Palm Ash

This study reports on the microstructure, compressive strength, and drying shrinkage of metakaolin (MK) based geopolymers produced by partially replacing MK by oil palm ash (OPA). The OPA was used as raw material producing different molar ratios of SiO₂/Al₂O₃ and CaO/SiO₂. The geopolymer samples were cured at 80°C for 1, 2, or 4 hours and kept at ambient temperature until testing. The compressi...

Photocatalytic Degradation of Dyes

TiO2-Based Photocatalytic Geopolymers for Nitric Oxide Degradation

This study presents an experimental overview for the development of photocatalytic materials based on geopolymer binders as catalyst support matrices. Particularly, geopolymer matrices obtained from different solid precursors (fly ash and metakaolin), composite systems (siloxane-hybrid, foamed hybrid), and curing temperatures (room temperature and 60 °C) were investigated for the same photocata...

Study of Metakaolin-Based Geopolymer with Addition of Polymer Admixtures

In the present work, metakaolin-based geopolymer including different polymer admixtures was studied. Different types of commercial polymer admixtures VINNAPAS® and polyethylene glycol of different relative molecular weight were used as polymer admixtures. The main objective of this work is to investigate the influence of different types of admixtures on the properties of metakaolin-based geopol...

Application-Oriented Chemical Optimization of a Metakaolin Based Geopolymer

In this study the development of a metakaolin based geopolymeric mortar to be used as bonding matrix for external strengthening of reinforced concrete beams is reported. Four geopolymer formulations have been obtained by varying the composition of the activating solution in terms of SiO₂/Na₂O ratio. The obtained samples have been characterized from a structural, microstructural and mechanical p...