Nano-sized Superlattice Clusters Created by Oxygen Ordering in Mechanically Alloyed Fe Alloys
نویسندگان
چکیده
منابع مشابه
Nano-sized Superlattice Clusters Created by Oxygen Ordering in Mechanically Alloyed Fe Alloys
Creating and maintaining precipitates coherent with the host matrix, under service conditions is one of the most effective approaches for successful development of alloys for high temperature applications; prominent examples include Ni- and Co-based superalloys and Al alloys. While ferritic alloys are among the most important structural engineering alloys in our society, no reliable coherent pr...
متن کاملStructural Characterization and Ordering Transformation of Mechanically Alloyed Nanocrystalline Fe-28Al Powder
The synthesis of nanocrystalline Fe3Al powder by mechanical alloying as well as the structural ordering of the synthesized Fe3Al particles during the subsequent thermal analysis were investigated. Mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. The synthesized powders were cha...
متن کاملXANES of Mechanically Alloyed Y-Fe System
We have measured X-ray absorption near edge structure (XANFS) of mechanically alloyed YzFe and YFez system as a fundion of milling time. An amorphous phase is obtained by mechanical alloying for 100 hours in the YzFe system and for 500 hours in the YFez system. In both systems the intensity of Fe Is-4pn transition grows up significantly with increasing the milling time and approaches to that of...
متن کاملstructural characterization and ordering transformation of mechanically alloyed nanocrystalline fe-28al powder
the synthesis of nanocrystalline fe3al powder by mechanical alloying as well as the structural ordering of the synthesized fe3al particles during the subsequent thermal analysis were investigated. mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. the synthesized powders were cha...
متن کاملNucleation mechanism of nano-sized NaZn13-type and α-(Fe,Si) phases in La-Fe-Si alloys during rapid solidification
The nucleation mechanism involving rapid solidification of undercooled La-Fe-Si melts has been studied experimentally and theoretically. The classical nucleation theory-based simulations show a competitive nucleation process between the α-(Fe,Si) phase (size approximately 10 to 30 nm) and the cubic NaZn13-type phase (hereinafter 1:13 phase, size approximately 200 to 400 nm) during rapid solidif...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2015
ISSN: 2045-2322
DOI: 10.1038/srep11772