Nano-Silver Ink of High Conductivity and Low Sintering Temperature for Paper Electronics
نویسندگان
چکیده
منابع مشابه
Dispensing of high concentration Ag nano-particles ink for ultra-low resistivity paper-based writing electronics.
Paper-based writing electronics has received a lot of interest recently due to its potential applications in flexible electronics. To obtain ultra-low resistivity paper-based writing electronics, we developed a kind of ink with high concentration of Ag Nano-particles (up to 80 wt%), as well as a related dispensing writing system consisting an air compressor machine and a dispenser. Additionally...
متن کاملStudy of die attach technologies for high temperature power electronics: Silver sintering and gold-germanium alloy
Silver sintering joints and AuGe soldering are promising technologies for high temperature (>200 C ambient) power electronics packaging. This paper presents the implementation of two silver-sintering processes with the one hand micrometer-scale silver particles, and on the other hand nano-meter-scale particles. Two substrates technologies have been investigated: A12O3 DBC and Si3N4 AMB. After t...
متن کاملMechanical Characterization of Ink-Jet Printed Ag Samples on Different Substrates
In this paper, the main activity was to investigate how different substrates, temperature of sintering and percentage of silver ink containing silver nanoparticles influence on Young’s modulus and hardness of printed silver thin samples. Samples were prepared by low cost ink-jet printing technique using Dimatix Material Printer on polyimide flexible substrate and slide glass. Characterization o...
متن کاملFacile synthesis of silver nanoparticles useful for fabrication of high-conductivity elements for printed electronics.
A facile synthesis of stable silver nanoparticles having a particle size of <10 nm is described. The synthesis involved reduction of silver acetate with a substituted hydrazine, such as PhNHNH2, in the presence of a 1-alkylamine, such as C16H33NH2, in toluene at 25-60 degrees C. Spin-coated thin films or printed electronic features of alkylamine-stabilized silver nanoparticles could be easily c...
متن کاملMicrowave Sintering of High Thermal Conductivity Aln
In this study, a combustion synthesized AlN powder was sintered using microwave as heating source. The microwave was 2.45 GHz and the sintering process was carried out in a single-mode cavity. The sintering temperature was between 1800°C and 2000°C with a power ranging from 400 to 700W. The as-synthesized AlN was ground to under 2μm and yttria was used as sintering aid. The effects of the amoun...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2019
ISSN: 1931-7573,1556-276X
DOI: 10.1186/s11671-019-3011-1