Mushy zone morphology during directional solidification of Pb-5.8 wt pct Sb alloy
نویسندگان
چکیده
منابع مشابه
Effect of Sb Addition on the Solidification of Deeply Undercooled Ag-28.1 wt. % Cu Eutectic Alloy
Ag-28.1 wt. % Cu eutectic alloy solidifies in the form of eutectic dendrite at undercooling above 76 K. The remelting and ripening of the original lamellar eutectics result in the formation of the anomalous eutectics in the final microstructure. The addition of the third element Sb (0.5 and 1 wt. %) does not change the growth mode, but enlarges the volume fraction of anomalous eutectics because...
متن کاملConvective instabilities during the solidification of an ideal ternary alloy in a mushy layer
DANIEL M. ANDERSON†, GEOFFREY B. McFADDEN, SAM R. CORIELL AND BRUCE T. MURRAY Department of Mathematical Sciences, George Mason University, Fairfax, VA 22030, USA Mathematical and Computational Sciences Division, National Institute of Standards and Technology, Gaithersburg, MD 20899, USA Metallurgy Division, National Institute of Standards and Technology, Gaithersburg, MD 20899, USA Department ...
متن کاملThe Mechanical Strength of Si Foams in the Mushy Zone during Solidification of Al–Si Alloys
The mechanical strength of an Al-30% Si alloy in the mushy zone was estimated by using a novel centrifugation apparatus. In the apparatus, the alloy melt was partially solidified, forming a porous structure made of primary Si platelets (Si foam) while cooling. Subsequently, pressure generated by centrifugal force pushed the liquid phase out of the foam. The estimated mechanical strength of the ...
متن کاملCellular arrays during upward solidification of Pb - 30 wt % T 1 alloys
2014 A quantitative study of the cellular or dendritic hexagonal arrays, obtained during upward solidification of Pb-30 wt% T1 alloys, is presented. These arrays are reconstituted by the Wigner-Seitz method which allows the determination of the primary spacing, the identification of the defects and the analysis of the disorganization of the interface structures by using concepts developed for t...
متن کاملLiquation and re-solidification in thermo-mechanically affected zone during friction stir spot welding of AZ91 alloy
The present research aims to study the liquation and re-solidification of liquid during friction stir spot welding of AZ91 alloy. Although friction stir spot welding is a solid-state process, the presence of Mg17Al12 intermetallic compounds results in liquation during the welding process. In this study, friction stir spot welding was performed with a tool rotational speed of 2500 rev/min and a ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallurgical and Materials Transactions A
سال: 2000
ISSN: 1073-5623,1543-1940
DOI: 10.1007/s11661-000-0144-9