Multilayer NIR reflective coatings on transparent plastic substrates from photopolymerizable nanoparticulate sols
نویسندگان
چکیده
منابع مشابه
Multilayer NIR re ̄ective coatings on transparent plastic substrates from photopolymerizable nanoparticulate sols
A new synthesis and processing route for preparing multilayer interference coatings on plastic substrates has been developed. For this purpose, alcoholic sols of surface modi®ed (3 glycidoxypropyltrimethoxysilane, GPTS) SiO2 and TiO2 particles with sizes of 10 and 4 nm, respectively, were synthesized. Layers were prepared by dip coating, subsequent UV curing (2.1 J/cm) and thermal post treatmen...
متن کاملIR-reflective Opaque Water-based Acrylic Coatings on White Pine Wood Substrates
Two sets of opaque water-based acrylic coatings were prepared with IR-reflective pigments and conventional pigments. The objective of this work was to determine the efficiency of IR-reflective pigments in limiting the heat buildup of opaque coating formulations. Experiments performed on PVC substrates revealed that IR-reflective pigments significantly decreased the temperature increase above ro...
متن کاملMinimax design of optically transparent and reflective coatings.
We consider the design problem of creating coatings that are either highly reflective or highly transparent. The goal is to create an optical element, consisting of planar dielectric layers, that reflects (or transmits) energy over a given range of wavelengths and angles of incidence. The approach that we take is to formulate the problem as a minimax optimization problem. We demonstrate that th...
متن کاملPlastic Deformation Induced by Nanoindentation Test Applied on ZrN/Si3N4 Multilayer Coatings
ZrN/Si3N4 multilayer coating that alternates with either nanocrystalline ZrN or amorphous Si3N4 interlayers was fabricated by reactively magnetron sputtering in an Ar-N2 mixture atmosphere. The thicknesses of the nanocrystalline ZrN and the amorphous Si3N4 interlayers are ~12.5 and 2.5 nm, respectively. The ZrN/Si3N4 coating exhibits a promoted hardness of 28.6 ± 1.2 GPa when compared to the bi...
متن کاملEllipsometry of light scattering from multilayer coatings.
A scatterometer is extended and allows us to perform ellipsometric measurements on scattered light in each direction of space. Experimental data are given for single thin-film layers and optical coatings and reveal unexpected results. The phenomena are investigated by means of the electromagnetic theories of surface and bulk scattering that emphasize the role of partial correlation and localize...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Thin Solid Films
سال: 1999
ISSN: 0040-6090
DOI: 10.1016/s0040-6090(99)00340-5