Multiaxial fatigue damage modelling at macro scale of Ti–6Al–4V alloy
نویسندگان
چکیده
منابع مشابه
Fatigue Performance of Medical Ti6Al4V Alloy after Mechanical Surface Treatments
Mechanical surface treatments have a long history in traditional engineering disciplines, such as the automotive or aerospace industries. Today, they are widely applied to metal components to increase the mechanical performance of these. However, their application in the medical field is rather rare. The present study aims to compare the potential of relevant mechanical surface treatments on th...
متن کاملTwo-time-scale fatigue modelling: application to damage
A temporal multiscale modelling applied to fatigue damage evolution in cortical bone is presented. Microdamage accumulation in cortical bone, ensued from daily activities, leads to impaired mechanical properties, in particular by reducing the bone stiffness and inducing fatigue. However, bone damage is also known as a stimulus to bone remodelling, whose aim is to repair and generate new bone, a...
متن کاملEvaluation of continuum damage at different temperatures for aluminum-silicon alloy of engine piston within low-cycle fatigue regime
In this article, the isothermal low-cycle fatigue continuum damage in the engine piston aluminum alloy has been evaluated at different temperatures. For this objective, experimental data of low-cycle fatigue tests on standard specimens were used at 280, 350 and 425°C. Based on the continuum damage mechanics method, the fatigue damage was calculated during cyclic loading. Obtained results, inclu...
متن کاملMultiaxial fatigue reliability analysis of railroad wheels
A general methodology for fatigue reliability degradation of railroad wheels is proposed in this paper. Both fatigue crack initiation and crack propagation life are included in the proposed methodology using previously developed multiaxial fatigue models by the same authors. A response surface method in conjunction with design of experiments is used to develop a closed form approximation of the...
متن کاملA New Energy-Critical Plane Damage Parameter for Multiaxial Fatigue Life Prediction of Turbine Blades
As one of fracture critical components of an aircraft engine, accurate life prediction of a turbine blade to disk attachment is significant for ensuring the engine structural integrity and reliability. Fatigue failure of a turbine blade is often caused under multiaxial cyclic loadings at high temperatures. In this paper, considering different failure types, a new energy-critical plane damage pa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Fatigue
سال: 2009
ISSN: 0142-1123
DOI: 10.1016/j.ijfatigue.2009.03.003