Multiaxial fatigue behavior of SLM Ti6Al4V alloy under different loading conditions
نویسندگان
چکیده
منابع مشابه
Linkage between Ductile Fracture and Extremely Low Cycle Fatigue of Inconel 718 under Multiaxial Loading Conditions
Ductile fracture and extremely low cycle fatigue (ELCF) [1] are two common failure modes in aircraft engines and turbomachinery designs [2]; however, the linkage between these two failure modes under multi-axial loading conditions has never been systematically studied. Inconel 718 (IN718) is one type of high temperature alloys widely used in turbomachines. Specially designed specimens and tests...
متن کاملSubstructure Model for Concrete Behavior Simulation under Cyclic Multiaxial Loading
This paper proposes a framework for the constitutive model based on the semi-micromechanical aspects of plasticity, including damage progress for simulating behavior of concrete under multiaxial loading. This model is aimed to be used in plastic and fracture analysis of both regular and reinforced concrete structures, for the framework of sample plane crack approach. This model uses multilamina...
متن کاملCrack Behavior of the Aluminum Alloy 2024 Under Fretting Conditions
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...
متن کاملFatigue Performance of Medical Ti6Al4V Alloy after Mechanical Surface Treatments
Mechanical surface treatments have a long history in traditional engineering disciplines, such as the automotive or aerospace industries. Today, they are widely applied to metal components to increase the mechanical performance of these. However, their application in the medical field is rather rare. The present study aims to compare the potential of relevant mechanical surface treatments on th...
متن کاملInverse first-order reliability method for probabilistic fatigue life prediction of composite laminates under multiaxial loading
Inverse first-order reliability method for probabilistic fatigue life prediction of composite laminates under multiaxial loading Yibing Xiang and Yongming Liu* Department of Civil and Environmental Engineering Clarkson University Potsdam NY.13699, USA Abstract: Multiaxial fatigue reliability is a challenging problem despite extensive progress made during the past few decades. Anisotropic materi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Fatigue & Fracture of Engineering Materials & Structures
سال: 2021
ISSN: 8756-758X,1460-2695
DOI: 10.1111/ffe.13518