Multiaxial Fatigue and Cracking Orientation of Forged AZ80 Magnesium Alloy

Kinetics of SIMA AZ80 Magnesium Alloy

Semi-solid feedstock of AZ80 magnesium alloy modified by [trace] rare-earth Y element 10 (0, 0.2, 0.4, 0.8 wt.%) were fabricated by [strain-induced melting activation] (SIMA) in the form of 11 extrusion and partial remelting. The effect of Y addition on the microstructure evolution of [the] 12 extruded and [isothermally heat] treated alloy was observed by [using an] optical microscope (OM), 13 ...

Microstructure-sensitive investigation of magnesium alloy fatigue

Fatigue behaviour and fractography of extruded AZ80 magnesium alloys in very high cycle regime

In order to investigate the fatigue properties of extruded magnesium alloy in very high-cycle regime, rotary bending fatigue test was performed in ambient atmosphere at room temperature using the hourglass shaped specimens of AZ80 alloys extruded (Fspecimen) and treated by an artificial aging after extrusion (T5-specimen). From the experimental results, both specimens show a clear step-wise S-N...

Tensile and fatigue behavior of AZ91D magnesium alloy

Recently magnesium alloys, owing to their low density and excellent specific strength have been attractive to designers as an advanced material for coping with energy conservation and environmental pollution regulations. Much of the recent developments of magnesium alloys and processes have been driven by the requirements of the aerospace industry, although some successful ones have found appli...

Hardness evolution of AZ80 magnesium alloy processed by HPT at different temperatures

Discs of an extruded AZ80 magnesium alloy were processed by high-pressure torsion (HPT) using 6.0 GPa up to 10 turns at different temperatures (296 K and 473 K). The disc surfaces and cross-sectional planes were examined before and after processing using scanning electron microscopy (SEM) and Vickers microhardness (Hv). The microhardness results at the surface show differences in the strength o...