Morphology, thermal stability and thermal degradation kinetics of cellulose-modified urea–formaldehyde resin
نویسندگان
چکیده
منابع مشابه
Thermal Degradation Kinetics of Sugarcane Bagasse and Soft Wood Cellulose
The properties of untreated sugar cane bagasse (SCB) and soft wood (SW) and their respective celluloses were investigated. The celluloses indicated improved crystallinity index values and decreased concentration of lignin and hemicellulose compared to their untreated counterparts. Three degradation models, Kissinger-Akahira-Sunose (KAS), Flynn-Wall-Ozawa (OFW), and Kissinger (KGR) methods were ...
متن کاملThermal Degradation and Stability of Accelerated-curing Phenol-formaldehyde Resin
In order to study the thermal stability of accelerated-curing PF resin, the curing behavior of fresh PF resin was investigated in the presence of single accelerator of methylolurea derivatives (MMU), magnesium hydrate (Mg(OH)2), 25% aqueous solution of sodium carbonate (Na2CO3), and propylene carbonate (PC). Also their optimum combination was added in fresh PF resin. The thermal stability of cu...
متن کاملThermal Properties and Thermal Degradation of Cellulose Tri-Stearate (CTs)
Cellulose tri-stearate (CTs) was synthesized employing trifluoroacetic anhydride (TFAA), stearic acid (SA), with microcrystal cellulose (MCC) and characterized with FT-IR and 1 H-NMR. The degree of substitution of CTs was determined by the traditional saponification method and 1 H-NMR. The thermal properties of CTs were investigated by the thermogravimetric analysis (TGA) under Ar flow in dynam...
متن کاملThermal stability and degradation kinetics of polystyrene/organically-modified montmorillonite nanocomposites.
Organically-modified montmorillonite (MMT) clays have been prepared using ammonium salts containing quinoline, pyridine, benzene, and styrenic groups. The nanocomposites were prepared by melt blending and the formation of nanocomposites was characterized using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Thermal stability and flammability were evaluated by thermogravimetr...
متن کاملMechanical and Thermal Properties of Chemically Modified Epoxy Resin
Diglycidyl ether of bisphenol-A (DGEBA), having number average molecular weight (Mn) 375, was modified by incorporating the hydroxyl terminated polybutadiene (HTPB) based prepolymer using isophorone diisocyanate as a coupling agent. To increase the compatibility between the epoxy resin and HTPB part, polar groups were introduced in the later to achieve physical and chemical interactions between...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bulletin of Materials Science
سال: 2016
ISSN: 0250-4707,0973-7669
DOI: 10.1007/s12034-016-1304-x