Modified F-criterion and its influence on potential crack deflection range
نویسندگان
چکیده
منابع مشابه
tt . - ) q Crack Branching and Deflection in Piezoelectric Materials
The problem of crack branching and deflection in bi-material system is considered in this paper. The combinations may be piezoelectric-piezoelectric, or piezoelectric and non-piezoelectric. Based on Stroh's formulation for anisotropic material, Green's functions for various bi-material combinations are presented within the framework of two-dimensional electro-elasticity, allowing the crack prob...
متن کاملQuasi-Static Crack Propagation by Griffith’s Criterion
We consider the propagation of a crack in a brittle material along a prescribed crack path and define a quasi-static evolution by means of stationary points of the free energy. We show that this evolution satisfies Griffith’s criterion in a suitable form which takes into account both stable and unstable propagation, as well as an energy balance formula which accounts for dissipation in the unst...
متن کاملRotor Crack Detection Approach Using Controlled Shaft Deflection
Rotating shafts are important and responsible components of many machines, such as power generation plants, aircraft engines, machine tool spindles, etc. A transverse shaft crack can occur due to cyclic loading, creep, stress corrosion, and other mechanisms to which rotating machines are subjected. If not detected early, the developing shaft crack can lead to a serious machine damage resulting ...
متن کامل[Proceeding] Crack deflection in brittle materials by Finite Fracture Mechanics
During their operation, modern aircraft engine components are subjected to increasingly demanding operating conditions, especially the high pressure turbine (HPT) blades. Such conditions cause these parts to undergo different types of time-dependent degradation, one of which is creep. A model using the finite element method (FEM) was developed, in order to be able to predict the creep behaviour...
متن کاملCrack nucleation criterion and its application to impact indentation in glasses
Molecular dynamics (MD) simulations are used to directly observe nucleation of median cracks in oxide glasses under indentation. Indenters with sharp angles can nucleate median cracks in samples with no pre-existing flaws, while indenters with larger indenter angles cannot. Increasing the tip radius increases the critical load for nucleation of the median crack. Based upon an independent set of...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Solids and Structures
سال: 2019
ISSN: 0020-7683
DOI: 10.1016/j.ijsolstr.2018.10.019