Modification with Melamine Formaldehyde and Melamine-Urea Formaldehyde Resin to Improve the Physical and Mechanical Properties of Wood
نویسندگان
چکیده
منابع مشابه
Rattan Cane Modified with Polyethylene Glycol Melamine-Urea-Formaldehyde Resin
To effectively improve the strength of Plectocomia pierreana rattan cane without reducing its toughness, the cane was impregnated with a new water-soluble melamine-urea-formaldehyde (MUF) resin modified with low-molecular-weight polyethylene glycol (PEG), marked as PMUF. The PMUF synthetic process was optimized using an orthogonal test L9(3). Results showed that the dimensional stability, densi...
متن کاملLiquefied Wood as a Partial Substitute of Melamine-urea- Formaldehyde and Urea-formaldehyde Resins
Maritime pine (Pinus pinaster) sawdust was used to produce liquefied wood by the polyhydric method with acid catalysis. The process was optimized to produce the highest amount of liquefied wood. Wood liquefied at 160oC for 90 min was used in the adhesion tests. The bond strength of veneer glued with ureaformaldehyde and melamine-urea-formaldehyde resins and several mixtures of liquefied wood wi...
متن کاملMelamine-modified urea formaldehyde resin for bonding particleboards
For the development of a cost-effective melamine-modified urea formaldehyde resin (MUF), the study evaluated the effects of reaction pH and melamine content on resin properties and bond performance of the MUF resin adhesive systems. Eight resins, each with three replicates, were prepared in a factorial experiment that included two formulation variables: two reaction pHs (i.e., 4.5 and 8.0) and ...
متن کاملEffects of Melamine Addition Stage on the Performance and Curing Behavior of Melamine-Urea-Formaldehyde (MUF) Resin
Three formaldehyde-based resins were prepared: urea-formaldehyde (UF) resin without melamine modifier (named UF0 resin) and melamineurea-formaldehyde (MUF) resins with melamine modifier added at two different synthesis stages (named MUF1 resin and MUF2 resin). The effects of the melamine addition stage on the performance and curing behavior of MUF resin were studied. Three-ply plywood bonded by...
متن کاملThe Effects of Adding Melamine at Different Resin Synthesis Points of Low Mole Ratio Urea-Melamine- Formaldehyde (UMF) Resins
Low mole ratio urea-melamine-formaldehyde (UMF) resins synthesized with 2.5% and 5.0% melamine levels added at the beginning, middle, and end points of the first alkaline step of the typical urea-formaldehyde (UF) resin synthesis procedure were compared with typical UMF resins synthesized with melamine additions made at the final alkaline step. Various resin analysis, particleboard preparation,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: BioResources
سال: 2016
ISSN: 1930-2126
DOI: 10.15376/biores.12.1.586-596