Modification of polyester fabric by treatment in alkaline solution
نویسندگان
چکیده
منابع مشابه
-plasma Treatment on Woven Plain Polyester Fabric in Adjusting Hydrophilicity
Hydrophilisation of polyester textile materials has been investigated over the last twenty years using low-pressure and atmospheric plasmas. According to these studies, wettability and capillarity of fabrics can be significantly improved depending on the process gas used. In the present study, the effects of low pressure O 2 and NH 3 plasma on the morphology and topometry of fabrics on four dif...
متن کاملCompression Properties of Polyester Needlepunched Fabric
In the present paper, a study of the effects of fabric weight, fiber cross-sectional shapes (round, hollow and trilobal) and presence of reinforcing material on the compression properties (initial thickness, percentage compression, percentage thickness loss and percentage compression resilience) of polyester needle punched industrial nonwoven fabrics is presented. It was found that for fabrics ...
متن کاملSericin based bioactive coating for polyester fabric
In this study, a process has been developed for durable coating of sericin on polyester. Pre modification of polyester with alkali (sodium hydroxide) has been carried out to incorporate polar entities on its inert surface. 10g/L of sericin with 30mL/L of glutaraldehyde, cured at 130°C for 2min has been optimized for its application on modified surface. Treated samples are tested for surface smo...
متن کاملHot Mercerizing of Cotton/Polyester Blend Fabric Effect of Alkali Treatment Temperature on Ttensile Properties , Weight Loss and Shrinkage of Fabric
The presence of defects in cold mercerizing of cotton goods led to the creation of a new method, called hot mercerizing in which caustic soda solution is used at a high temperature. Hot mercerizing is successfully used in cotton blended with some other fibers. In cotton/polyester blend fabrics, this treatment serves a dual purpose: subjectively, it imparts a silklike 


soft handle to ...
متن کاملHot Mercerizing of Cotton/Polyester Blend Fabric Effect of Alkali Treatment Temperature on Ttensile Properties , Weight Loss and Shrinkage of Fabric
The presence of defects in cold mercerizing of cotton goods led to the creation of a new method, called hot mercerizing in which caustic soda solution is used at a high temperature. Hot mercerizing is successfully used in cotton blended with some other fibers. In cotton/polyester blend fabrics, this treatment serves a dual purpose: subjectively, it imparts a silklike soft handle to the po...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tekstilna industrija
سال: 2019
ISSN: 0040-2389
DOI: 10.5937/tekstind1903050r