Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime
نویسندگان
چکیده
منابع مشابه
Biaxial High Cycle Fatigue of a Type 304L Stainless Steel: Cyclic Strains and Crack Initiation Detection by Digital Image Correlation
A series of biaxial High Cycle Fatigue tests at room temperature is performed to build up an extensive and well-documented database. The testing specimen is a maltese cross thinned in its centre with non homogeneous strain/stress fields. The experimental protocol uses exclusively full-field strain measurements. The strains (cyclic and residual) as well as the crack initiation detection are obta...
متن کاملAn Outrun Competition of Corrosion Fatigue and Stress Corrosion Cracking on Crack Initiation in a Compressor Blade
First row rotating blades of four axial-flow compressors were prematurely fractured. Previous investigations showed that the site atmosphere contains corrosive compounds which lead to an increase in possibility of pitting on the blades. It was also revealed that the crack was originated from two corrosion pits. Thus, this work is conducted to ascertain which of fatigue or stress corrosion crack...
متن کاملSide Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملEffect of Weld Metal Microstructure on the Fatigue and Corrosion-Fatigue Properties of GTA-Welded 304 Stainless Steel
In this research, two different filler metals, ERNiCrMo-3 and ER309L, were used for developing different microstructure, austenite (γ) and austenite and ferrite (γ+δ) in the weld metal and fatigue properties of welded samples were evaluated in the air and sea water environments. Microstructural studies indicated a good agreement between predicted microstructures via schiffler diagram and metall...
متن کاملEffect of Weld Metal Microstructure on the Fatigue and Corrosion-Fatigue Properties of GTA-Welded 304 Stainless Steel
In this research, two different filler metals, ERNiCrMo-3 and ER309L, were used for developing different microstructure, austenite (γ) and austenite and ferrite (γ+δ) in the weld metal and fatigue properties of welded samples were evaluated in the air and sea water environments. Microstructural studies indicated a good agreement between predicted microstructures via schiffler diagram and metall...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Science
سال: 2018
ISSN: 0010-938X
DOI: 10.1016/j.corsci.2018.01.034