Modelling Dynamic Recrystallization of A356 Aluminum Alloy during Hot Deformation
نویسندگان
چکیده
The flow stress and dynamic recrystallization behavior of A356 aluminum alloy was studied, with a strain rate ranging from 0.001 s?1 to 1 temperature 300 500 °C. Both the true stress–strain curves microstructure examination indicated that occurred during isothermal compression. A physical model based on Arrhenius equation developed, this can accurately predict fraction Finally, implemented in FEM software Forge, evolution simulated well.
منابع مشابه
Microstructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملDynamic Recrystallization by Necklace Mechanism During Hot Deformation of 316 Stainless Steel
The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is 316 stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °C with strain rates of 0.01-1s-1. The result shows that at the tempera...
متن کاملIn situ study of dynamic recrystallization and hot deformation behavior of a multiphase titanium aluminide alloy
multiphase titanium aluminide alloy Klaus-Dieter Liss, Thomas Schmoelzer, Kun Yan, Mark Reid, Matthew Peel, Rian Dippenaar, and Helmut Clemens Australian Nuclear Science and Technology Organisation, PMB 1, Menai, New South Wales 2234, Australia Department of Physical Metallurgy and Materials Testing, Montanuniversität, A-8700 Leoben, Austria Faculty of Engineering, University of Wollongong, Wol...
متن کاملPorosity Prediction in Aluminum A356 Alloy Castings
A comprehensive methodology that takes into account alloy solidification, shrinkage-driven interdendritic fluid flow, hydrogen precipitation, and porosity evolution has been developed for the prediction of microporosity fraction in aluminum A356 alloy castings. The mathematical models presented are implemented in a computational framework consistent with those of commercial casting codes, allow...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2022
ISSN: ['2075-4701']
DOI: https://doi.org/10.3390/met12091407