MODELING FATIGUE LIFE OF POLYCRYSTALLINE STRUCTURAL ALLOYS UNDER A COMBINED EFFECT OF LOW- AND HIGH-CYCLE FATIGUE MECHANISMS
نویسندگان
چکیده
منابع مشابه
Ultra-Low Cycle Fatigue Fracture Life of a Type of Buckling Restrained Brace
Buckling restrained braced frames (BRBFs) for seismic load resistance have been widely used in recent years. One of the key requirements for a buckling restrained brace is to sustain large plastic deformations under severe ground motions. The core of a buckling restrained brace is prone to fatigue fracture under cyclic loading. The earthquake induced fracture type of the core plate in a bucklin...
متن کاملA Combined High and Low Cycle Fatigue Model for Life Prediction of Turbine Blades
Combined high and low cycle fatigue (CCF) generally induces the failure of aircraft gas turbine attachments. Based on the aero-engine load spectrum, accurate assessment of fatigue damage due to the interaction of high cycle fatigue (HCF) resulting from high frequency vibrations and low cycle fatigue (LCF) from ground-air-ground engine cycles is of critical importance for ensuring structural int...
متن کاملEnergy-Based Prediction of Low-Cycle Fatigue Life of CK45 Steel and SS316 Stainless Steel
In this paper, low cycle fatigue life of CK45 steel and SS316 stainless steel under strain-controlled loading are experimentally investigated. In addition, the impact of mean strain and strain amplitude on the fatigue life and cyclic behavior of the materials are studied. Furthermore, it is attempted to predict fatigue life using energy and SWT damage parameters. The experimental results demons...
متن کاملEffect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy
The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...
متن کاملHigh-cycle Fatigue in Micron-scale Structural Films of Polycrystalline Silicon: a Reaction-layer Failure Mechanism
A study has been made of high-cycle fatigue in 2-μm thick structural films of ntype, polycrystalline silicon for MEMS applications. Using an “on-chip” test structure resonating at ~40 kHz, such thin-film polysilicon is shown to display “metal-like” stress-life fatigue behavior in room air environments, with failures occurring after lives in excess of 10 cycles at stresses as low as half the fra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Problems of Strength and Plasticity
سال: 2019
ISSN: 1814-9146
DOI: 10.32326/1814-9146-2019-81-3-305-323