MODEL OF SHELL FRACTURE WITH SURFACE CRACKS
نویسندگان
چکیده
منابع مشابه
Mixed Mode Fracture Analysis of Multiple Interface Cracks
This paper contains a theoretical formulation of multiple interface cracks in two bonded dissimilar half planes subjected to in-plane traction. The distributed dislocation technique is used to construct integral equations for a dissimilar mediums weakened by several interface cracks. These equations are of Cauchy singular type at the location of dislocation, which are solved numerically to obta...
متن کاملCracks Analysis in Zavin Concrete Dam Using Fracture Mechanics Approach
Most of the existing concrete dams are subjected to cracking. These cracks are caused by various factors such as construction practices, curing, loads and volume change of mass concrete which reduce the efficiency, failure or instability of concrete dams. Using fracture mechanics as a new method to estimate stability and durability of concrete dams is recommended in scientific publications in w...
متن کاملEngineering Critical Assessments of Marine Pipelines with 3D Surface Cracks Considering Weld Mismatch
Offshore pipelines are usually constructed by the use of girth welds, while welds may naturally contain flaws. Currently, fracture assessment procedures such as BS 7910 are based on the stress-based methods and their responses for situations with large plastic strain is suspicious. DNV-OS-F101 with limited modifications proposes a strain-based procedure for such plastic loads. In this paper 3D ...
متن کاملThe initiation and persistence of cracks in Enceladus ’ ice shell
Introduction: The remarkable eruptions from cracks in Enceladus’ South Polar Terrain (SPT) provide a unique window into the interior of an icy satellite. Here we revisit the processes that create cracks and prevent them from freezing in light of the confirmation that Enceladus has a global ocean [1,2] and analyses of the gravity field that indicate that the ice shell is thinnest beneath the SPT...
متن کاملEstimation of the Stress Intensity Factors for Surface Cracks in Spherical Electrode Particles Subject to Phase Separation
Experiments have frequently shown that phase separation in lithium-ion battery electrodes could lead to the formation of mechanical defects, hence causing capacity fading. The purpose of the present work has been to examine stress intensity factors for pre-existing surface cracks in spherical electrode particles during electrochemical deintercalation cycling using both analytical and numerical ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Problems of Strength and Plasticity
سال: 2006
ISSN: 1814-9146
DOI: 10.32326/1814-9146-2006-68-1-45-52