Mode II and Mixed Mode Delamination Growth in Composite Materials Using Peridynamic Theory
نویسندگان
چکیده
منابع مشابه
Comprehensively simulating the mixed-mode progressive delamination in composite laminates
Gao, Zhenyuan MSAA, Purdue University, May 2015. Comprehensively Simulating the Mixed-Mode Progressive Delamination in Composite Laminates. Major Professor: Wenbin Yu. Delamination, or interlaminar debonding, is a commonly observed failure mechanism in composite laminates. It is of great significance to comprehensively simulate the mixed-mode progressive delamination in composite structures bec...
متن کاملMixed-Mode Bending Method for Delamination Testing
A mixed—mode delamination test procedure was developed combining double cantilever beam (DCB) mode I loading and end-notch fixture (ENF) mode II loading on a split unidirectional laminate. By loading with a lever, a single applied load simultaneously produces mode I and mode II bending loads on the specimen. This mixed-mode bending (MMB) test was analyzed using both finite-element procedures an...
متن کاملMixed-Mode Stress Intensity Factors for Surface Cracks in Functionally Graded Materials Using Enriched Finite Elements
Three-dimensional enriched finite elements are used to compute mixed-mode stress intensity factors (SIFs) for three-dimensional cracks in elastic functionally graded materials (FGMs) that are subject to general mixed-mode loading. The method, which advantageously does not require special mesh configuration/modifications and post-processing of finite element results, is an enhancement of previou...
متن کاملMixed-mode I/II Interlaminar Fracture of CF/PEI Composite Material
Failures in composite materials occur mainly due to interlaminar fracture, also called delamination, between laminates. This indicates that characterizing interlaminar fracture toughness is the most effective factor in the fracture of composite materials. This study reports investigation on mixed-mode interlaminar fracture behaviour in woven carbon fibre/polyetherimide (CF/PEI) thermoplastic co...
متن کاملMixed Mode Crack Propagation of Zirconia/Nickel Functionally Graded Materials
Zirconia-nickel functionally graded materials were obtained by powder metallurgy technique. The microstructure, residual stress, fracture toughness and Vickers hardness were investigated. Mixed-mode fracture response of YSZ /Ni functionally graded materials was examined utilizing the three point bending test and finite element method (Cosmos/M 2.7). The results show that the stress intensity fac...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Structural Integrity
سال: 2020
ISSN: 2452-3216
DOI: 10.1016/j.prostr.2020.11.028