Mixed-mode fatigue crack growth using cohesive zone modeling
نویسندگان
چکیده
منابع مشابه
A cohesive model of fatigue crack growth
We investigate the use of cohesive theories of fracture, in conjunction with the explicit resolution of the near-tip plastic fields and the enforcement of closure as a contact constraint, for the purpose of fatiguelife prediction. An important characteristic of the cohesive laws considered here is that they exhibit unloadingreloading hysteresis. This feature has the important consequence of pre...
متن کاملShort and Large Crack , Mixed - Mode Fatigue - Crack Growth Thresholds in Ti - 6 Al - 4 V
There are few experimental results to date describing the crack-propagation threshold behavior of short fatigue cracks under multiaxial loading conditions. To address this need, in the present study, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size and shape are reported for a Ti-6Al-4V turbine blade alloy, heat treated to two widely different microstructu...
متن کاملA Cohesive Zone Model for Crack Growth Simulation in AISI 304 Steel
Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...
متن کاملQuasistatic Crack Growth for a Cohesive Zone Model with Prescribed Crack Path
In this paper we study the quasistatic crack growth for a cohesive zone model. We assume that the crack path is prescribed and we study the time evolution of the crack in the framework of the variational theory of rate-independent processes.
متن کاملMixed-mode, high-cycle fatigue-crack growth thresholds in Ti– 6Al–4V: Role of small cracks
There have been few studies to date describing fatigue-crack propagation thresholds under mixed-mode loading conditions in the presence of cracks, that are small as compared to the characteristic microstructural dimensions. To address this need, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size is reported for a Ti-6Al-4V turbine blade alloy with a fine-gra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Engineering Fracture Mechanics
سال: 2020
ISSN: 0013-7944
DOI: 10.1016/j.engfracmech.2020.107234