Mixed-mode elastic-plastic fracture of 2024-T351 aluminum alloy.
نویسندگان
چکیده
منابع مشابه
Fatigue of Friction Stir Welded 2024-T351 Aluminium Alloy
Fatigue failure characteristics of friction stir welds in 13mm gauge 2024-T351 plate have been assessed. Failure occurred from either the weld region (nugget/flow arm) or from the material immediately surrounding the weld. Fatigue failure from the surrounding material was essentially conventional, initiating from large S-phase intermetallic particles and growing in a macroscopic mode I manner. ...
متن کاملTensile properties and fracture locations of friction-stir-welded joints of 2017-T351 aluminum alloy
Friction stir welding (FSW) is a new and promising welding process that can produce low-cost and high-quality joints of heat-treatable aluminum alloys because it does not need consumable filler materials and can eliminate some welding defects such as crack and porosity. In order to demonstrate the friction stir weldability of the 2017-T351 aluminum alloy and determine optimum welding parameters...
متن کاملElastic-plastic Mode-ii Fracture of Adhesive Joints
A numerical study of the elastic-plastic mode-II fracture of adhesive joints is presented in this paper. A traction-separation law was used to simulate the mode-II interfacial fracture of adhesively-bonded end-notched flexure (E.N.F.) specimens loaded in three-point bending, with extensive plastic deformation accompanying failure. The fracture parameters for the traction-separation law were det...
متن کاملEffect of Aging Condition on Semisolid Cast 2024 Aluminum Alloy
2024 Aluminum alloy was squeezed cast by the Gas Induced Semi Solid (GISS) process. Effect of artificial aging on microstructure and mechanical properties of this alloy was studied in the present work. The solutionized specimens were aged hardened at temperatures of 175°C, 200°C, and 225°C under various time durations. The highest hardness of about 77.7 HRE was attained from specimen aged at th...
متن کاملCrack Behavior of the Aluminum Alloy 2024 Under Fretting Conditions
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1985
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.51.2129