Mix design, properties and cost analysis of fly ash-based geopolymer foam
نویسندگان
چکیده
منابع مشابه
ALKALI Activated FLY-ASH Based Geopolymer Concrete
Considering the increasing demand for developing alternative construction materials, due to the growing environmental concerns, this paper discusses the feasibility of alkali activated geo-polymer concrete, as a future construction material. The main objective of this study involves observation of structural behaviours of the fresh fly ash-based geo-polymer concrete, understanding the basic mix...
متن کاملFly Ash-Based Geopolymer Mortar Incorporating Bottom Ash
This paper presents the results of study on effect of various parameters on mechanical properties of fly ash-based geopolymer mortar with bottom ash as partial or full replacement for sand. Compressive strength of samples with 10% bottom ash (BA) was comparable to those with only sand. Further increase in bottom ash content decreased the compressive strength. However, the reverse tendency occur...
متن کاملAcid Resistance of Fly ash based Geopolymer mortars
Geopolymers are a new promising binder manufactured by activation of a solid aluminosilicate source material with a highly alkaline activating solution and aided by heat. Fly ash, considered to be a waste material is rich in silica and alumina and hence can be used as a source material for manufacture of Geopolymers. These binders have been reported to achieve high early strength and better dur...
متن کاملMechanical Properties and Microstructure of Class C Fly Ash-Based Geopolymer Paste and Mortar
This paper presents workability, compressive strength and microstructure for geopolymer pastes and mortars made of class C fly ash at mass ratios of water-to-fly ash from 0.30 to 0.35. Fluidity was in the range of 145-173 mm for pastes and 131-136 mm for mortars. The highest strengths of paste and mortar were 58 MPa and 85 MPa when they were cured at 70 °C for 24 h. In XRD patterns, unreacted q...
متن کاملFly Ash-based Geopolymer Lightweight Concrete Using Foaming Agent
In this paper, we report the results of our investigation on the possibility of producing foam concrete by using a geopolymer system. Class C fly ash was mixed with an alkaline activator solution (a mixture of sodium silicate and NaOH), and foam was added to the geopolymeric mixture to produce lightweight concrete. The NaOH solution was prepared by dilute NaOH pellets with distilled water. The ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Construction and Building Materials
سال: 2015
ISSN: 0950-0618
DOI: 10.1016/j.conbuildmat.2015.01.063