Microwave Synthesis of Ti<sub>4</sub>O<sub>7</sub> or AlN Nanoparticles by Rapid Carbothermal Reduction Process
نویسندگان
چکیده
منابع مشابه
Synthesis of Ti4O7 Nanoparticles by Carbothermal Reduction Using Microwave Rapid Heating
The polymer electrolyte fuel cell (PEFC) is an attractive power generation method from the perspective of environmental protection. Carbon is usually used as a catalyst support in PEFC, but it is oxidized under high electrical potential conditions. Ti4O7 is expected as a new catalyst support because of its high electrical conductivity and chemical resistivity. Though Ti4O7 as a catalyst support...
متن کاملSynthesis of HfB2 Powders by Carbothermal Reduction
In this research, solid state carbothermal synthesis of HfB2 Nano powders was investigated. For this purpose, HfO2,H3BO3, carbon active or phenolic resin were used as raw materials for carbothermal reaction. After 2-4 hours of milling the raw materials by a planetary ball in an ethanol media, the mixture was heat dried and pressed in to disks under pressure of 20-30 bar. The disks were then pla...
متن کاملA rapid microwave route for the synthesis of ZnS nanoparticles
ZnS nanoparticles were synthesized via a simple surfactant free microwave route. In this synthesis, thioacetamide was used as sulfur source. The effects of different parameters such as type of zinc precursor, time and power of irradiation on the morphology and particle size of the products have been investigated. The nanostructures were characterized by ...
متن کاملRoute to GaN and VN assisted by carbothermal reduction process.
A route to prepare nitrides, such as GaN, VN, and other nitrides, is reported. The reaction pathway involves a two-step process by using the as-synthesized a-C3N3.69 as precursor. The route is so potent that a series of nitrides can be directly synthesized from their oxides at moderate temperatures. A striking feature of this method lies in that a-C3N3.69 is found to play double roles as both c...
متن کاملIn Situ Spectroscopic Analysis of the Carbothermal Reduction Process of Iron Oxides during Microwave Irradiation
The effects of microwave plasma induction and reduction on the promotion of the carbothermal reduction of iron oxides (α-Fe2O3, γ-Fe2O3, and Fe3O4) are investigated using in situ emission spectroscopy measurements during 2.45 GHz microwave processing, and the plasma discharge (such as CN and N2) is measured during microwave E-field irradiation. It is shown that CN gas or excited CN molecules co...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Petroleum Institute
سال: 2018
ISSN: 1346-8804,1349-273X
DOI: 10.1627/jpi.61.88