Microwave-Assisted Polyol Synthesis of Water Dispersible Red-Emitting Eu3+-Modified Carbon Dots
Eu3+-modified carbon dots (C-dots), 3-5 nm in diameter, were prepared, functionalized, and stabilized via a one-pot polyol synthesis. The role of Eu2+/Eu3+, the influence of O₂ (oxidation) and H₂O (hydrolysis), as well as the impact of the heating procedure (conventional resistance heating and microwave (MW) heating) were explored. With the reducing conditions of the polyol at the elevated temp...
متن کاملMicrowave-assisted polyol synthesis of carbon nitride dots from folic acid for cell imaging
A green, one-step microwave-assisted polyol synthesis was employed to prepare blue luminescent carbon nitride dots (CNDs) using folic acid molecules as both carbon and nitrogen sources. The as-prepared CNDs had an average size of around 4.51 nm and could be well dispersed in water. Under excitation at 360 nm, the CNDs exhibited a strong blue luminescence and the quantum yield was estimated to b...
متن کاملMagnetic gold nanotriangles by microwave-assisted polyol synthesis.
Simple approaches to synthesize hybrid nanoparticles with magnetic and plasmonic functionalities, with high control of their shape and avoiding cytotoxic reactants, to target biomedical applications remain a huge challenge. Here, we report a facile, fast and bio-friendly microwave-assisted polyol route for the synthesis of a complex multi-material consisting of monodisperse gold nanotriangles a...
متن کاملHighly Luminescent Water-Dispersible NIR-Emitting Wurtzite CuInS2/ZnS Core/Shell Colloidal Quantum Dots
Copper indium sulfide (CIS) quantum dots (QDs) are attractive as labels for biomedical imaging, since they have large absorption coefficients across a broad spectral range, size- and composition-tunable photoluminescence from the visible to the near-infrared, and low toxicity. However, the application of NIR-emitting CIS QDs is still hindered by large size and shape dispersions and low photolum...
متن کاملLuminescent properties of novel red-emitting phosphor: Gd2O2CN2:Eu3+
Eu 3+ -doped Gd2O2CN2 was firstly synthesized by a classical solid-state reaction of Li2CO3, Eu2O3 and GdF3 under NH3 gas flow in the presence of graphite at low firing temperature. Powder X-ray diffraction (XRD) analysis indicated that Gd2O2CN2: Eu 3+ crystallizes in a trigonal-type structure with space group P-3m1. Gd2O2CN2: Eu 3+ shows a sharp red emission band peaking at 626 nm under excita...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2016
ISSN: 1996-1944
DOI: 10.3390/ma10010025