Microstructures and mechanical properties of Al-Mg2Si-Si alloys resistance spot welded with Al-Si interlayers

Effects of Alloying Additions and Cooling Rate on the Microstructures and Mechanical Properties of the Cast Al-Mg-Si Alloys

Cast aluminum alloys are widely applied for the transportation industry. Alloys with silicon and magnesium as the main alloying elements are the most important of the aluminum casting alloys because of their high fluidity. However, Al-Si-Mg alloys have exhibited medium strength level at room and, especially, at elevated temperature. Recently, new casting alloys with high magnesium and silicon h...

The Role of Mg2Si in the Corrosion Behavior of Al-Si-Mg Alloys for Pressureless Infiltration

The role of Mg2Si in the electrochemical behavior of Al-Si-Mg aluminum alloys has been studied using four experimental aluminum alloys with variations in the Si/Mg molar ratio (A1-0.12, A2-0.49, A3-0.89, A4-1.05), in neutral aerated 0.1M NaCl solutions. Accordingly, the corrosion potential in open circuit (Eoc) and polarization resistance (Rp) were measured. Results show that the augment in Si/...

Precipitation Hardening of Al–Si–Mg Alloys

Effects of Complex Modification by Sr–Sb on the Microstructures and Mechanical Properties of Al–18 wt % Mg2Si–4.5Cu Alloys

This research was carried out to investigate the influence of Sr–Sb on the microstructures and mechanical properties of Al–18 wt % Mg2Si–4.5Cu alloys. After the addition of 0.2 wt % Sr–Sb, the morphologies of primary Mg2Si transformed from equiaxed dendrite to cube in as-cast alloys and the average size of primary Mg2Si decreased from ~50 to ~20 μm. The shape of eutectic Mg2Si changed from Chin...

The Mechanical Strength of Si Foams in the Mushy Zone during Solidification of Al–Si Alloys

The mechanical strength of an Al-30% Si alloy in the mushy zone was estimated by using a novel centrifugation apparatus. In the apparatus, the alloy melt was partially solidified, forming a porous structure made of primary Si platelets (Si foam) while cooling. Subsequently, pressure generated by centrifugal force pushed the liquid phase out of the foam. The estimated mechanical strength of the ...