Microstructure of V–4Cr–4Ti alloy after low-temperature irradiation by ions and neutrons
نویسندگان
چکیده
منابع مشابه
MICROSTRUCTURE OF AlSi17Cu5 ALLOY AFTER OVERHEATING OVER LIQUIDUS TEMPERATURE
J. Piątkowski The Silesian University of Technology, Faculty of Materials Science and Metallurgy, Katowice, Poland R. Wieszała, The Silesian University of Technology, Faculty of Transport, Katowice, Poland The paper presents microstructure tests of alloy AlSi17Cu5. In order to disintegrate the primary grain of silicon the so-called time-temperature transformation TTT was applied which was based...
متن کاملEffect or Inoculation on Microstructure and Properties of Low C-Mn and Low Alloy Steels
Effect of the addition of various inoculants on the morphology and mechanical properties of low C-Mn and low alloy steel samples is studied by thermal and mechanical processing of the samples after solidification. According to the results obtained from metallographic studies with the electron microscope and microanalysis with x-rays, the distribution of inoculating agents in the steel matrix is...
متن کاملMicrostructure and High Temperature Deformation Behavior of Cast 310S Alloy
High temperature deformation behavior of cast 310S stainless steel has been investigated in this study by performing tensile and compression tests at temperatures from 900 to 1200C. Rectangular ingots of which the dimensions were 350×350×100 in millimeter were cast using vacuum induction melting. Phase equilibrium was calculated using the FactSage®, thermodynamic software and database. Thermal ...
متن کاملEffects of Heavy-ion Irradiation on Micr at Moderate Temperatures*
V-4 wt.% Cr-4 wt.% Ti alloy is a promising candidate material for first-wall and structural applications in magnetic fusion reactors. In the past, fast neutron sources were used to evaluate postirradiation properties of fusion candidate materials. The recent shutdowns of the Fast Flux Test Facility (FFTF) and the Experimental Breeder Reactor (EBR-II) left U.S. researchers without local experime...
متن کاملEvaluation of microstructure and mechanical properties of 410NiMo as an overlay layer on low alloy steel
The aim of this study is to reach an increased service life for parts using in sour environment by weld overlaying process. In this investigation, two successive layers of ER410NiMo were clad on low alloy steel substrates. To reduce the likelihood of Hydrogen Induced Cracking (HIC) and producing stable hydrogen traps, Post Weld Heat Treatment (PWHT) was conducted. Microstructural analysis, X-ra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Nuclear Materials
سال: 1998
ISSN: 0022-3115
DOI: 10.1016/s0022-3115(98)00159-7