Microstructure, Metal-Mold Reaction and Fluidity of Investment Cast-TiAl Alloys
نویسندگان
چکیده
منابع مشابه
Effect of Mold Preheating on the Microstructure of the Investment Cast Astm F-75 Implant Alloy
The ASTM F-75 (Co-28%Cr-6%Mo) is widely used as a biocompatible alloy in medicinefor manufacturing implants. In this study, effect of mold preheating on the as-cast microstructure of thealloy was investigated using the solid investment casting process. Several mold preheating temperaturesof 550, 700, 850 and 1000 °C were selected at the same melt superheat. The samples were characterizedby opti...
متن کاملEffect of Mold Preheating on the Microstructure of the Investment Cast Astm F-75 Implant Alloy
The ASTM F-75 (Co-28%Cr-6%Mo) is widely used as a biocompatible alloy in medicine for manufacturing implants. In this study, effect of mold preheating on the as-cast microstructure of the alloy was investigated using the solid investment casting process. Several mold preheating temperatures of 550, 700, 850 and 1000 °C were selected at the same melt superheat. The samples were characterized by ...
متن کاملModeling of TiAl Alloy Grating by Investment Casting
The investment casting of TiAl alloys has become the most promising cost-effective technique for manufacturing TiAl components. This study aimed to investigate a series of problems associated with the investment casting of TiAl alloys. The mold filling and solidification of this casting model were numerically simulated using ProCAST. Shrinkage porosity was quantitatively predicted by a built-in...
متن کاملMicrostructure of Retrievals Made from Standard Cast HC-CoCrMo Alloys
During the past decade, self-mating metal bearings based on cobalt– chromium–molybdenum (CoCrMo) alloys have become very popular in total hip replacements and hip resurfacings. This led to a market share of more than 35 % for metal-on-metal (MoM) bearings in the United States before several cases of high wear with biologic consequences led to a sharp drop in popularity. In part, these failures ...
متن کاملCharacterization of the Dendritic Microstructure of Investment Cast Alloy 718
The as-cast alloy 718 shows a multiphasic structure which consists of dendrites, carbides and Laves phases. The amount, size, shape, and dispersion of these phases affect the properties and the processing which follows, This structure was characterized by measurements of volume fraction, size, dispersion, and shape factor of carbide and Laves phases. Secondary arm spacing and Vickers hardness w...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2004
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.45.536