MICROSTRUCTURE, MECHANICAL AND TRIBOLOGICAL BEHAVIOR OF THE TiAlVN COATINGS
نویسندگان
چکیده
منابع مشابه
Microstructure, Mechanical and Tribological Properties of Reactive Magnetron Sputtered Titanium Carbide Coatings
This study describes the correlation between the microstructure, mechanical and tribological properties of Ti1-xCx coatings (with x being in the range of 0-1), deposited by reactive magnetron sputtering from a Ti target in Ar/C2H2 mixtures at ~200 °C. The mechanical and tribological properties were found to strongly depend on the chemical composition and the microstructure present. Very dense s...
متن کاملEffect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملTribological behavior of sputter-deposited MoSX/Ni coatings
AbstractSputtered MoS2 coatings have been mostly used as a solid lubricant. In this investigation, MoSx/Ni composite coatings with Ni contents varying from 0 to 22 % were deposited onto steel substrate using a DC magnetron sputter process. The MoS2/Ni ratio in the coatings was controlled by sputtering the composite targets. The composition, microstructure, and mechanical properties of the...
متن کاملINFLUENCE OF MECHANICAL ALLOYING AND LEAD CONTENT ON MICROSTRUCTURE, HARDNESS AND TRIBOLOGICAL BEHAVIOR OF 6061 ALUMINIUM ALLOYS
In the present work, one batch of prealloyed 6061Al powder was processed by mixing and another one was ball milled with varying amount of lead content (0-15 vol. %). These powders were compacted at 300MPa and sintered at 590˚C under N2. The instrumented hardness and the young’s modulus of as-sintered 6061Al-Pb alloys were examined as a function of lead content and processing route. The we...
متن کاملMechanical and tribological behavior of silicon nitride and silicon carbon nitride coatings for total joint replacements.
Total joint replacements currently have relatively high success rates at 10-15 years; however, increasing ageing and an active population places higher demands on the longevity of the implants. A wear resistant configuration with wear particles that resorb in vivo can potentially increase the lifetime of an implant. In this study, silicon nitride (SixNy) and silicon carbon nitride (SixCyNz) coa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Metallurgica Slovaca
سال: 2018
ISSN: 1338-1156,1335-1532
DOI: 10.12776/ams.v24i4.1187