Microstructure and Toughness of 950 MPa High Strength Weld Metals.
نویسندگان
چکیده
منابع مشابه
New Developments with C–Mn–Ni High Strength Steel Weld Metals — Part A. Microstructure
The relationship between alloying content, microstructure and properties has been studied for high strength steel weld metals with 7 to 9 wt. % nickel. Neural network modelling suggested that manganese reductions lead to large impact toughness increases and that nickel must be added in a controlled manner with respect to manganese in order toincrease impact toughness. Carbon additions were pred...
متن کاملSize distribution of oxides and toughness of steel weld metals
The trend in strong weld metals is towards microstructures dominated by low carbon martensite. The role of oxide particles introduced into the metal during welding then becomes uncertain. The particles do not seem to affect the nucleation or growth of martensite. This is probably because this phase forms at relatively large driving forces and therefore does not rely on heterogeneous nucleation ...
متن کاملMicrostructural characterisation of as-deposited and reheated weld metal — High Strength Steel Weld Metals
The problems encountered with the interpretation of martensite and the various forms of bainite that are found in high strength steel weld metals have been addressed. Field emission gun scanning electron microscopy was found to overcome resolution difficulties often met with light optical microscopy and conventional scanning electron microscopy. The various microstructural constituents were cha...
متن کاملChanges in toughness at low oxygen concentrations in steel weld metals
Oxides in steel weld metals can initiate fracture or can improve toughness by influencing the development of beneficial microstructures. In this work, the authors conducted experiments in which the oxygen concentration was varied from 20 to 560 ppmw (parts per million by weight) in weld metals with tensile strength in the range 580–780 MPa. It is demonstrated that low and medium strength weld m...
متن کاملUnderstanding Mechanical Properties of Novel High Strength Steel Weld Metals Through High-Resolution Microstructural Investigations
Shielded metal arc welding and submerged arc welding were used to prepare experimental weld metals with variations in nickel, manganese and carbon contents. The weld metals contained Ni between 6.6 and 10.5 wt. %, Mn between 0.5 and 2.0 wt. % while carbon was varied between 0.03 and 0.11 wt. %. Mechanical properties were found to be sensitive to alloying content. However once the optimum level ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 2000
ISSN: 0288-4771
DOI: 10.2207/qjjws.18.496