Microstructure and Residual Stress in AMS 6308 Steel after Vacuum Carburizing and Gas Quenching
نویسندگان
چکیده
منابع مشابه
Gas and Vacuum Carburizing
The solution algorithm used in CarbTool is based on the finite difference method (FDM), and the code is developed using Microsoft Visual C++ in Window OS. The tool has been built on the concept of the carbon flux at the surface between the gas and steel is to be specified by the user. The outputs of CarbTool are the carbon concentration distribution profile inside the steel part and the surfa...
متن کاملEvolution of Microstructure and Residual Stress under Various Vibration Modes in 304 Stainless Steel Welds
Simultaneous vibration welding of 304 stainless steel was carried out with an eccentric circulating vibrator and a magnetic telescopic vibrator at subresonant (362 Hz and 59.3 Hz) and resonant (376 Hz and 60.9 Hz) frequencies. The experimental results indicate that the temperature gradient can be increased, accelerating nucleation and causing grain refinement during this process. During simulta...
متن کاملModeling of acetylene pyrolysis under steel vacuum carburizing conditions in a tubular flow reactor.
In the present work, the pyrolysis of acetylene was studied under steel vacuum carburizing conditions in a tubular flow reactor. The pyrolysis temperature ranged from 650 degrees C to 1050 degrees C. The partial pressure of acetylene in the feed mixture was 10 and 20 mbar, respectively, while the rest of the mixture consisted of nitrogen. The total pressure of the mixture was 1.6 bar. A kinetic...
متن کاملEngineering the residual stress state and microstructure of stainless steel with mechanical surface treatments
Four mechanical surface treatments have been considered for the application to austenitic stainless steel structures. Shot peening (SP), laser shock peening (LSP), ultrasonic impact treatment (UIT) and water jet cavitation peening (WJCP), also known as cavitation shotless peening (CSP), have been applied to 8 mm thick Type 304 austenitic stainless steel coupons. This study considers the merits ...
متن کاملSCC of 2304 Duplex Stainless Steel—Microstructure, Residual Stress and Surface Grinding Effects
The influence of surface grinding and microstructure on chloride induced stress corrosion cracking (SCC) behavior of 2304 duplex stainless steel has been investigated. Grinding operations were performed both parallel and perpendicular to the rolling direction of the material. SCC tests were conducted in boiling magnesium chloride according to ASTM G36; specimens were exposed both without extern...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Physica Polonica A
سال: 2016
ISSN: 0587-4246,1898-794X
DOI: 10.12693/aphyspola.130.953