Microstructure and hot deformation behavior of FeMnAlCMo steel
نویسندگان
چکیده
منابع مشابه
Effects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. 
The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite r...
متن کاملEffects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite reg...
متن کاملeffects of carbon on the microstructure and hot deformation behavior
the effects of carbon content on the dynamic and static softening mechanisms of ti microalloy steels were investigated both in ferrite and austenite regions. the results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. this is due to the ti(cn) and tic precipitates and also the free carbon content. in the ferrite regio...
متن کاملHot Deformation Behavior of 17-7 PH Stainless Steel
To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملEVALUATING HOT DEFORMATION BEHAVIOR OF W360 TOOL STEEL BY HOT COMPRESSION TEST
In this research, the hot deformation behavior of W360 tool steel was investigated using hot compression test at 1000-1200°C and strain rates of 0.001, 0.01, 0.1, and 1 s-1. According to the results, dynamic recrystallization was found the most important restoration factor of this alloy during hot deformation. Recrystallization was enhanced with an increase in temperature and strain rate. Also,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Research and Technology
سال: 2020
ISSN: 2238-7854
DOI: 10.1016/j.jmrt.2020.02.069