Microstructure and fracture characteristics in reactive sintering TiAl intermetallic compound.
نویسندگان
چکیده
منابع مشابه
Reactive Sintering of TiAl - Ti 5 Si 3 Lnsitu Composites
TiAl with between 0 and 20 volume percent (v%)Ti5Si3 was produced by reactive sintering of cofd pressed compacts of elemental Ti, Al and Si powder mixtures at 7OO0C for 15 minutes in vacuum. The results show that adding Si to Ti and A1 reduces the swelling associated with reactive sintering of TiAI, as composites containing more than 5 vYoTigSi3 densified during reactive sintering. However, com...
متن کاملHIGH-TEMPERATURE FRACTURE AND FATIGUE RESISTANCE OF A DUCTILE b-TiNb REINFORCED g-TiAl INTERMETALLIC COMPOSITE
ÐThe high-temperature fatigue-crack propagation and fracture resistance of a model g-TiAl intermetallic composite reinforced with 20 vol.% ductile b-TiNb particles is examined at elevated temperatures of 650 and 8008C and compared with behavior at room temperature. TiNb reinforcements are found to enhance the fracture toughness of g-TiAl, even at high temperatures, from about 12 to 040 MPa m, a...
متن کاملANALYTICAL DATA FOR NiO REDUCTION AND Al3Ni2 INTERMETALLIC COMPOUND FORMATION
In this research, the nickel oxide was dissolved in cryolite at temperatures of 880, 940 and 1000°C. In order to reduce the nickel oxide, aluminum was added to the salt. Simultaneously the nickel oxide was reduced and Al3Ni2 intermetallic compound was formed. In the duration intervals of 2.5-40 minutes samples of the salt and metallic phases were taken. The variation of the nickel content in me...
متن کاملDENSIFICATION AND MICROSTRUCTURE CHARACTERISTICS OF A PREALLOYED ALPHA BRASS POWDER PROCESSED BY LIQUID PHASE SINTERING
The rapidly solidified prealloyed alpha brass powder with a size range of 40 to 100 μm produced by water atomization process was consolidated using liquid phase sintering process. The relationships between sintering temperature, physic-mechanical properties and microstructural characteristics were investigated. Maximum densification was obtained at 930 °C, under 600 MPa compacting pressure,...
متن کاملMagnetic phase transitions in intermetallic CeCuGe compound
Electrical and magnetic properties of CeCuGe were investigated through electrical resistivity, thermal conductivity and magnetization measurements in the temperature range 2–300 K. Magnetization measurements indicate a paramagnetic to ferromagnetic transition at TZ10 K, in agreement with previous work. There are two distinct paramagnetic regimes: At high-T the magnetic moment per cerium is 2.50...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1997
ISSN: 0451-5994,1880-8018
DOI: 10.2464/jilm.47.521