Microstructure and Ferroelectric Properties of Low Temperature Sintering PMN-PNN-PZT Ceramics with Sintering Temperature

Low-temperature sintering of MnO2-doped PZT–PZN Piezoelectric ceramics

The effect of MnO2 addition on the microstructural evolution and piezoelectric properties of low temperature sinterable PZT–PZN ceramics was investigated. When a small amount of MnO2 (≤0.5 wt% ) was added, the Mn ions were homogeneously dissolved in the PZT– PZN ceramics, leading to full densification at a temperature as low as 930 °C. However, the further addition of MnO2 hindered the densific...

LOW-TEMPERATURE SINTERING AND MICROWAVE DIELECTRIC PROPERTIES OF (Zn0.65Mg0.35)TiO3-CaTiO3 CERAMICS WITH H3BO3 ADDITION

Low-melting H3BO3, acting as sintering aid, was used to reduce the sintering temperature of 5 wt.% CaTiO3-doped (Zn0.65Mg0.35)TiO3 ceramics. The sintering behaviors, microstructures and microwave dielectric properties with different amounts of H3BO3 addition were investigated. The results showed that H3BO3 additive was very effective for lowering the sintering temperature and improving the bulk...

Practical classes " Ceramics & Colloids " : TP 3 Sintering 1 TP 3 - Ceramics : Sintering and Microstructure

After the initial molding of the ceramic, whether by slip casting or dry pressing, it is still necessary to densify the compacted powder samples (green bodies) to form a continuous 3D structure and thus to get ceramic pieces appropriate for the selected application. Usually this is done by a sintering process which is a consolidation and densification step of the granular compact through the ac...

Spark Plasma Sintering of Negative Temperature Coefficient Thermistor Ceramics

Effect of Sintering Temperature on Structural, Dielectric, and Magnetic Properties of Multiferroic YFeO3 Ceramics Fabricated by Spark Plasma Sintering

Based on precursor powders with a size of 200-300 nm prepared by the low-temperature solid reaction method, phase-pure YFeO₃ ceramics are fabricated using spark plasma sintering (SPS) at different temperatures. X-ray diffraction (XRD) and scanning electron microscopy (SEM) reveal that the high-purity YFeO₃ ceramics can be prepared using SPS, while the results from X-ray photoelectron spectrosco...