Microstructure and Fatigue Properties of Nodular Cast Iron at Low Frequency Cyclic Loading

Fatigue Behaviour of Synthetic Nodular Cast Irons

A. Vaško, L. Trško, R. Konečná, Faculty of Mechanical Engineering, University of Žilina, Žilina, Slovak Republic The paper shows the influence of charge composition on microstructure, fatigue properties and failure micromechanisms of nodular cast irons. The additive of metallurgical silicon carbide (SiC) in analysed specimens increases the content of ferrite in the matrix, decreases the size of...

The Microsegregation Pattern of Aluminum and Silicon in the Matrix Microstructure of the Nodular Cast Irons

The Microsegregation Pattern of Aluminum and Silicon in the Matrix Microstructure of the Nodular Cast Irons

Investigating the Effect of Titanium Addition on the Microstructure and Mechanical Properties of Ni-Hard 4 Cast Iron

Ni-Hard4 white cast iron is excellent wear resistant material and has been widely used in wearaffected equipment operated under extreme conditions, such as in mineral processing, cement, copper and iron manufacturing. In this study the effect of titanium addition (1.2, 0.7 and 0.2 wt.%) to the Ni-hard 4 cast iron with the nominal composition of Si= 1.5%, Mn=0.5%, C=3%, P=0.05%, S= 0.05%, Mo= 0....

Investigating the Effect of Titanium Addition on the Microstructure and Mechanical Properties of Ni-Hard 4 Cast Iron

Ni-Hard4 white cast iron is excellent wear resistant material and has been widely used in wearaffected equipment operated under extreme conditions, such as in mineral processing, cement, copper and iron manufacturing. In this study the effect of titanium addition (1.2, 0.7 and 0.2 wt.%) to the Ni-hard 4 cast iron with the nominal composition of Si= 1.5%, Mn=0.5%, C=3%, P=0.05%, S= 0.05%, Mo= 0....