Microstructure and activation volume of Cu-6wt%Zn brass processed by equal channel angular pressing
نویسندگان
چکیده
The generation of a high density twins few tens nanometers in size can enhance both strength and ductility. present work aims to produce highly twinned microstructure Cu-6wt% Zn alloy moderate stacking fault energy (SFE) by equal channel angular pressing (ECAP) using die with angles ϕ=110° Ψ=0. X ray diffraction (XRD) shows that defects is stored up 2 passes then recovery takes place. EBSD imaging reveals fibrous microstructure. Grains close 100 nm are formed. Strain rate sensitivity (SRS) was investigated compression nanoindentation (NI). Compression curves show deformation occurs slipping contribution hardening. A shear bands revealed during ECAP tests. activation volume V* NI the range 70b3 - 100b3, consistent emission dislocations from grain boundaries twin experimental values were compared those expected defect densities.
منابع مشابه
Microstructure Evolution in High Purity Aluminum Single Crystal Processed by Equal Channel Angular Pressing (ECAP)
Aluminum single crystal with 99.999% purity was deformed at room temperature by equal channel angular pressing (ECAP) up to 16 passes. Grain size and misorientation of processed samples were quantitatively characterized by TEM and EBSD. The results show that the refinement efficiency of high purity aluminum single crystal was poor in the initial stage. Extrusion by fewer ECAP passes (n ≤ 8) res...
متن کاملDevelopment Microstructure and Mechanical Properties of Commercially Pure Titanium Processed by Equal Channel Angular Pressing and Cold Drawing
Equal channel angular pressing has been used to refine the grain size of commercially pure titanium (grade 2) as well as other metals and alloys. Titanium grade 2 is usually processed at about 350 °C because it lacks sufficient ductility at lower temperatures. The warm processing temperature limits the capability of the equal channel angular pressing technique in improving the strength of titan...
متن کاملSize effect in equal channel angular pressing (ECAP) process
The influence of the sample size (diameter while keeping the length constant) in equal channel angular pressing (ECAP) of pure aluminum is examined using finite element method (FEM) and experiment. Different sized aluminum rods were processed via ECAP and the effect of sample size on the strain homogeneity, process load, and the ratio of the friction to the total force were evaluated. The resul...
متن کاملRe-strengthening in AA6063 Alloy During Equal Channel Angular Pressing
Equal channel angular pressing (ECAP) is carried out using two different configurations for the exit channel of the ECAP die, i.e., relieved and choked, with angles of 0.2 °. It is found that using a die with relieved exit channel, the sample was extruded for 6 passes with no surface cracks and an average cell size of 727 nm and a fraction of high angle grain boundaries of 54 % were achieved. M...
متن کاملMicrostructure and Texture Evolution of the Al-20Sn Alloy Processed by Equal-Channel Angular Pressing using RouteC
1Instituto de Investigaciones en Materiales, Universidad Nacional Autónoma de México, Circuito exterior S/N, Cd. Universitaria, A.P. 70-360, Coyoacán, C.P. 04510, Mexico 2Laboratoire Procédés et Ingénierie en Mécanique et Matériaux, CNRS UMR 8006, ENSAM, 151, bd de Hôpital 75013, Paris, France 3Laboratorio de Microscopía Electrónica, Universidad Autónoma Metropolitana, Unidad Iztapalapa. San Ra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Alloys and Compounds
سال: 2023
ISSN: ['0925-8388', '1873-4669']
DOI: https://doi.org/10.1016/j.jallcom.2023.171974