Microstructural evaluation of hydrogen embrittlement and successive recovery in advanced high strength steel
نویسندگان
چکیده
منابع مشابه
Hydrogen Embrittlement of High Strength Steel Electroplated with Zinc-cobalt Alloys
Slow strain rate tests were performed on quenched and tempered AISI 4340 steel to measure the extent of hydrogen embrittlement caused by electroplating with zinc-cobalt alloys. The effects of bath composition and pH were studied and compared with results for electrodeposited cadmium and zinc-10%nickel. It was found that Zinc-1%cobalt alloy coatings caused serious hydrogen embrittlement (EI 0.63...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملHydrogen Embrittlement Behavior of a 1700 MPa-Class Ultrahigh Strength Steel Containing Hydrogen Traps
Eiji Akiyama , Songjie Li , Yuuji Kimura , Kaneaki Tsuzaki , Nobuyoshi Uno c a National Institute for Materials Science 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan b School of Materials Science and Engineering, University of Science and Technology Beijing, No. 30 Xueyuan Road, Hidian Zone, Beijing 100083, China c Nippon Steel and Sumikin Metal Products Co, Ltd, SA Bldg., 17-12 Kiba 2-chome, ...
متن کاملInvestigation of structural changes in resistance spot welding of advanced high strength steel DP590
The structural and hardness developed in advanced high-strength steel DP590 have been investigated with the help of optical microscopy and scanning electron microscopy on resistance spot welded specimens. The hardness diagram of the weld sections was prepared by microhardness test and the temperature peak and heat distribution were simulated by menas of the Abaqus software. The results show tha...
متن کاملInvestigation of structural changes in resistance spot welding of advanced high strength steel DP590
The structural and hardness developed in advanced high-strength steel DP590 have been investigated with the help of optical microscopy and scanning electron microscopy on resistance spot welded specimens. The hardness diagram of the weld sections was prepared by microhardness test and the temperature peak and heat distribution were simulated by menas of the Abaqus software. The results show tha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Processing Technology
سال: 2019
ISSN: 0924-0136
DOI: 10.1016/j.jmatprotec.2018.09.039