Microstructural Characterization of Nb-Al Base ODS Alloys
نویسندگان
چکیده
منابع مشابه
Part I. The Microstructural Evolution in Ti-Al-Nb O 1 Bcc Orthorhombic Alloys
Phase transformations and the resulting microstructural evolution of near-Ti2AlNb and Ti-12Al38Nb O 1 bcc orthorhombic alloys were investigated. For the near-Ti2AlNb alloys, the processing temperatures were below the bcc transus, while, for Ti-12Al-38Nb, the processing temperature was supertransus. Phase evolution studies showed that these alloys contain several constituent phases, namely, bcc,...
متن کاملPhase Equilibria in Prototype Nb-Pd-Hf-Al Alloys
The phase equilibria in two prototype alloys with nominal compositions 60Nb-20Pd-10Hf-10Al and 40Nb-30Pd-15Hf-15Al (in at. pct) are investigated using scanning electron microscopy and X-ray diffraction. The alloys were heat treated at 1200 °C and 1500 °C for 200 hours each. The phase analysis revealed that the alloys were, for the most part, in the three-phase equilibrium between (Nb), Pd2HfAl,...
متن کاملReduction in Defect Content of ODS Alloys
Oxide dispersion strengthened (ODS) alloys prepared by mechanical alloying (MA) and subsequent consolidation are of increasing interest for potential application in components for use in power generation and furnace applications. After MA, canned alloy powders are usually subjected to a series of heat treatments. These heat treatments, particularly those at higher temperatures, last long enough...
متن کاملConfirming the Composition of Shape Memory Alloys by Microstructural Characterization
It is well known that the properties of shape memory alloys, such as binary Ni-Ti (nitinol), are very sensitive to composition.[1-3] Especially on the Ni-rich side of stoichiometry, the martensite/austenite phase transformation temperature decreases abruptly when Ni is increased only a few tenths of a weight percent.[4] In ternary high temperature shape memory alloys (HTSMAs) containing Pt, Pd,...
متن کاملReduction in Defect Content in ODS Alloys
In order to develop FeCrAl-based ODS alloy tubing with the coarse, high aspect ratio, appropriately oriented grain structures likely to deliver enhanced high temperature (1100C) hoop creep strength compared to conventionally formed ODS alloy tubing, flow forming techniques were explored in a European funded programme. The evolution of microstructure in PM2000 alloy tubing formed by warm flow fo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Science Forum
سال: 2010
ISSN: 1662-9752
DOI: 10.4028/www.scientific.net/msf.654-656.436