Microstructural Characteristics of Dynamic Recrystallization and Its Comparison with Static Recrystallization
نویسندگان
چکیده
منابع مشابه
Microstructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملStudy on Static Recrystallization Process in Duplex Stainless Steel 2205
Steel 2205 is one of the most famous duplex stainless steels. The microstructure of this steel composed of ferrite and austenite in similar amount. Therefore, in order to improve mechanical properties through microstructure, thermo mechanical processes such as controlled hot rolling and forging should be applied. It is not possible to employ the usual heat treatment. It shows the importance of ...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملPREDICTION OF CRITICAL STRESS AND STRAIN FOR THE ONSET OF DYNAMIC RECRYSTALLIZATION IN PLAIN CARBON STEELS
The aim of the present study is the prediction of critical conditions (including critical strain and flow stress) for the initiation of dynamic recrystallization during thermo-mechanical processing of plain carbon steels. For this propose, torsion tests were conducted at different temperature (1050, 1100 and 1150˚C) and strain rates (0.002, 0.02 and 0.2/s). All flow curves showed a peak st...
متن کاملDynamic Recrystallization and Hot Workability of 316LN Stainless Steel
Chaoyang Sun 1,*, Yu Xiang 1, Qingjun Zhou 2, Denis J. Politis 3, Zhihui Sun 1,* and Mengqi Wang 1 1 School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China; [email protected] (Y.X.); [email protected] (M.W.) 2 Capital Aerospace Machinery Company, Beijing 100076, China; [email protected] 3 Department of Mechanical Engineering, Imperial Co...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1984
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.70.15_2073