Microstructural changes in a Zn–Al eutectoid alloy modified with 2 wt.% Cu after superplastic deformation
نویسندگان
چکیده
منابع مشابه
Superplasticity of a fine-grained Mg–1.5 wt% Gd alloy after severe plastic deformation
The strain rate sensitivity (SRS) of Mg–1.5 wt% Gd processed by conventional extrusion and 2 passes of simple shear extrusion (SSE) was investigated by shear punch testing. Shear punch tests were conducted at initial shear strain rates in the range of 0.003–0.3 s-1 and at temperatures in the range of 573–773 K. A fine-grained microstructure with an average grain size of about 2.5 µm, obtained a...
متن کاملMicrostructural Evolution and Dynamic Softening Mechanisms of Al-Zn-Mg-Cu Alloy during Hot Compressive Deformation
The hot deformation behavior and microstructural evolution of an Al-Zn-Mg-Cu (7150) alloy was studied during hot compression at various temperatures (300 to 450 °C) and strain rates (0.001 to 10 s-1). A decline ratio map of flow stresses was proposed and divided into five deformation domains, in which the flow stress behavior was correlated with different microstructures and dynamic softening m...
متن کاملAchieving microstructures prone to superplastic deformation in an Al - Zn - Mg - Cu alloy by equal channel angular pressing
An Al-Zn-Mg-Cu alloy without Sc or Zr additions was subjected to overaging and processing by equal channel angular pressing, obtaining a grain size of ∼160 nm and a fraction of high-angle boundaries of 56%. The high elongations attained at high strain rate (10-10 s) and low test temperature (250-300 oC) are attributed to the formation of new recrystallized grains, ∼500 nm in size, during heatin...
متن کاملMicrostructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation
Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...
متن کاملCo-Precipitation, Strength and Electrical Resistivity of Cu–26 wt % Ag–0.1 wt % Fe Alloy
Both a Cu-26 wt % Ag (Fe-free) alloy and Cu-26 wt % Ag-0.1 wt % Fe (Fe-doping) alloy were subjected to different heat treatments. We studied the precipitation kinetics of Ag and Cu, microstructure evolution, magnetization, hardness, strength, and electrical resistivity of the two alloys. Fe addition was incapable of changing the precipitation kinetics of Ag and Cu; however, it decreased the siz...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Research and Technology
سال: 2020
ISSN: 2238-7854
DOI: 10.1016/j.jmrt.2020.03.086