Microstructural analysis of Ta-containing NiCoCrAlY bond coats deposited by HVOF on different Ni-based superalloys
نویسندگان
چکیده
منابع مشابه
Microstructural aspects of fatigue in Ni-base superalloys.
Nickel-base superalloys are primarily used as components in jet engines and land-based turbines. While compositionally complex, they are microstructurally simple, consisting of small (50-1000 nm diameter), ordered, coherent Ni(3)(Al,Ti)-type L1(2) or Ni(3)Nb-type DO(22) precipitates (called γ(') and γ(''), respectively) embedded in an FCC substitutional solid solution consisting primarily of Ni...
متن کاملMechanical Properties and Microstructural Evolution of Ta/TaNx Double Layer Thin Films Deposited by Magnetron Sputtering
Crystalline tantalum thin films of about 500nm thickness were deposited on AISI 316L stainless steel substrate using magnetron sputtering. To investigate the nano-mechanical properties of tantalum films, deposition was performed at two temperatures (25°C and 200°C) on TaNx intermediate layer with different N2/Ar flow rate ratio from 0 to 30%. Nano-indentation was performed to obtain the mechani...
متن کاملEffects of Cu on the microstructural and mechanical properties of sputter deposited Ni-Ti thin films
The microstructure of sputter deposited Ti-rich Ni-Ti thin films doped with Cu in the range 020.4 at.% and annealed for 1 h at 500 and 600°C has been investigated and correlated with the mechanical properties of the films measured by depth-sensing nanoindentation. X-ray diffraction analysis showed the microstructural evolution of Ni-Ti thin films when doped with Cu and annealed at different tem...
متن کاملEffect of Grinding Parameters on the Fracture Toughness of WC–10Co–4Cr Coating Deposited by HVOF
Nowadays, application of cermet coatings deposited by High-Velocity Oxygen-Fuel (HVOF) has received considerable attention in a variety of industries. Carbide coatings have high surface roughness, so it is essential to grind the coated surface. The present investigation studied the effect of simultaneous changes in the grinding parameters including the depth of cut, feed rate and cutting sp...
متن کاملON THE FORMATION OF STRAY GRAINS IN DIRECTIONALLY-SOLIDIFIED NI-BASED SUPERALLOYS WITH VARYING CROSS SECTIONS
Formation of stray grain defects particularly around re-entrant features of the turbine blade airfoils is one of the major problems in directional and single crystal solidification processes. In this work, directional solidification tests of the GTD-111 Ni-based superalloy were conducted at different withdrawal velocities of 3, 6 and 9 mm.min-1 using various stepped cylindrical and cubic design...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Surface and Coatings Technology
سال: 2018
ISSN: 0257-8972
DOI: 10.1016/j.surfcoat.2018.09.025