Microstructural Analysis of Mechanically Milled Nanocrystalline Fe Powder
نویسندگان
چکیده
منابع مشابه
Structural Characterization and Ordering Transformation of Mechanically Alloyed Nanocrystalline Fe-28Al Powder
The synthesis of nanocrystalline Fe3Al powder by mechanical alloying as well as the structural ordering of the synthesized Fe3Al particles during the subsequent thermal analysis were investigated. Mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. The synthesized powders were cha...
متن کاملAtomic-level observation of disclination dipoles in mechanically milled, nanocrystalline Fe.
Plastic deformation of materials occurs by the motion of defects known as dislocations and disclinations. High-resolution transmission electron microscopy was used to directly reveal the individual dislocations that constitute partial disclination dipoles in nanocrystalline, body-centered cubic iron that had undergone severe plastic deformation by mechanical milling. The mechanisms by which the...
متن کاملstructural characterization and ordering transformation of mechanically alloyed nanocrystalline fe-28al powder
the synthesis of nanocrystalline fe3al powder by mechanical alloying as well as the structural ordering of the synthesized fe3al particles during the subsequent thermal analysis were investigated. mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. the synthesized powders were cha...
متن کاملMicrostructural Evolution of Dy2O3-TiO2 Powder Mixtures during Ball Milling and Post-Milled Annealing
The microstructural evolution of Dy₂O₃-TiO₂ powder mixtures during ball milling and post-milled annealing was investigated using XRD, SEM, TEM, and DSC. At high ball-milling rotation speeds, the mixtures were fined, homogenized, nanocrystallized, and later completely amorphized, and the transformation of Dy₂O₃ from the cubic to the monoclinic crystal structure was observed. The amorphous transf...
متن کاملAnalysis of Mechanically Milled Exchange Coupled Nanocomposite Permanent Magnets
Nanocomposite permanent magnets have recently evoked wide interest because of their interesting properties. They usually consist of a hard magnetic phase having superior coercivities and a soft magnetic phase having improved values of magnetization and when they are coupled together, we get a permanent magnet with enhanced values of both the parameters and thus can be put to a lot of applicatio...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materia Japan
سال: 2003
ISSN: 1340-2625,1884-5843
DOI: 10.2320/materia.42.877