Micromagnetic simulations of first-order reversal curve (FORC) diagrams of framboidal greigite
نویسندگان
چکیده
منابع مشابه
Magnetic Properties of Fe49Co33Ni18Nanowire ArraysStudied by First-Order Reversal Curve Diagrams
Fe49Co33Ni18 nanowire arrays (175 nm in diameter and lengths ranging from 5 to 32μm) were fabricated into nanopores of hard-anodized aluminum oxide templates using pulsed ac electrodeposition technique. Hysteresis loop measurements indicated that increasing the length decreases coercivity and squareness values (from 274 Oe and 0.58 to200 Oe and 0.105, respective...
متن کاملCharacterization of hematite (a-Fe2O3), goethite (a-FeOOH), greigite (Fe3S4), and pyrrhotite (Fe7S8) using first-order reversal curve diagrams
[1] First-order reversal curve (FORC) diagrams have become a standard tool in rock magnetism, yet magnetite is the only magnetic mineral that is well characterized using FORC diagrams. We present FORC diagrams for predominantly single-domain (SD) synthetic aluminous hematite (a-Fe2-xAlxO3) and goethite (a-(FeAl)OOH) and natural greigite (Fe3S4) and pyrrhotite (Fe7S8) to constrain interpretation...
متن کاملmagnetic properties of fe49co33ni18nanowire arraysstudied by first-order reversal curve diagrams
fe49co33ni18 nanowire arrays (175 nm in diameter and lengths ranging from 5 to 32μm) were fabricated into nanopores of hard-anodized aluminum oxide templates using pulsed ac electrodeposition technique. hysteresis loop measurements indicated that increasing the length decreases coercivity and squareness values (from 274 oe and 0.58 to200 oe and 0.105, respectively), indicating the increase in m...
متن کاملFirst-order reversal-curve diagrams and reversible magnetization
First-order reversal curve ~FORC! diagrams have recently been used for the characterization of magnetic systems in both geology and physics. However, the FORC distribution involves a mixed second derivative which reduces the reversible component of the magnetization to zero. As a result, the FORC distribution is not properly normalized. Furthermore, the calculation of the FORC distribution beco...
متن کاملمطالعه برهمکنش مغناطواستاتیک نانووایرهای کبالت-آهن با استفاده از دیاگرامهای first order reversal curves (forc)
در این تحقیق برای اولین بار از قالب آلومینای آندی که به روش آندایز سخت با الکترولیت اسید اگزالیک در ولتاژ130 ولت تولید شده بود به عنوان قالب برای ساخت نانو سیمهای آلیاژی fe0.5co0.5استفاده شد. برای مطالعه ی میزان و شدت برهمکنش های مغناطواستاتیک بین آرایه ی نانوسیمها از سیستم آنالیز forc که با مشارکت و پشتیبانی شرکت مغناطیس دقیق کویر برای اولین بار در غرب آسیا طراحی و ساخته شده است، استفاده گردید...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Geophysical Journal International
سال: 2020
ISSN: 0956-540X,1365-246X
DOI: 10.1093/gji/ggaa241