Micro-abrasion-corrosion Maps of 316L Stainless Steel in Artificial Saliva
نویسندگان
چکیده
منابع مشابه
Micro-abrasion-corrosion maps of 316L stainless steel in artificial saliva
The role of salivary media is essential during mastication and ingestion processes; yet it can hinder the performance of foreign materials in the oral cavity. The aim of this study was to examine the effects of applied load and applied electrical potential on the tribo-corrosion mechanisms of 316L stainless steel in an environment similar to oral cavity conditions. 316L stainless steel is a mat...
متن کاملMicro abrasion-corrosion of AISI 316L stainless steel
In this study, the synergistic effects of abrasion and corrosion on AISI 316L stainless steel have been investigated using a micro-abrasion test rig. A series of results from abrasioncorrosion tests conducted using the micro-abrasion rig are presented. AISI 316L stainless steel has been studied under both pure abrasion and abrasion-corrosion conditions simulated by either distilled water or 3.5...
متن کاملCORROSION RESISTANCE OF TiN COATED 316L STAINLESS STEEL IN ARTIFICIAL PHYSIOLOGICAL SOLUTION
The corrosion behavior of TiN coated 316L stainless steel in an artificial physiological solution was investigated by means of an electrochemical test. Two different PVD methods were used for film deposition: cathodic arc and reactive magnetron sputtering. The dependence of the corrosion resistance on the main deposition parameters (nitrogen pressure, substrate bias) was analyzed. For a better ...
متن کاملLiquid Metal Corrosion of 316L Stainless Steel, 410 Stainless Steel, and 1015 Carbon Steel in a Molten Zinc Bath
Corrosion tests of 1015 low-carbon steel and two stainless steels (410 and 316L) were conducted in a pure zinc bath (99.98 wt pct Zn) in order to better understand the reaction mechanisms that occur during the degradation of submerged hardware at industrial general (batch) galvanizing operations. Through this testing, it was found that, in general, 316L stainless steel showed the best dissoluti...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Bio- and Tribo-Corrosion
سال: 2015
ISSN: 2198-4220,2198-4239
DOI: 10.1007/s40735-015-0015-y