Method of operational life’s increasing of transport’s parts due to usage of coatings based on epoxy matrix modified by maleinic anhydride with improved thermal physical properties

The use of a new method operational life increase the transport means parts due to introduction polymer-based modified materials has been substantiated in paper under discussion. It is shown that matrices based on epoxy diane oligomers quite promising direction protective coatings formation. Some active additives have applied improve properties preliminary stage their maleinic anhydride modifier containing interphase interaction functional groups as well. Epoxy oligomer used main component for matrix composite hardener polyethelenepolyamine link compositions enabling harden at room temperature. choice thermal-physical developed substantiated. found form material or coating with improved it necessary apply following ratio: q = 0,5 pts.wt. per 100 ЕД-20. In this case formed where, comparing nonmodified matrix, indices glass transition temperature are being increased from Тс 327 К tо 335 К, heat resistance (by Martenson) Т 341 362 and thermal coefficient linear expansion range temperatures ∆Т 303…423 decreased α 9,9 ×10-5 К-1 4,4 К-1. proved content its small fraction (q pts.wt.) activated processes CM structure formation, resulted number both physical chemical bonds polymer volume unit. This process will involve gel degree CM, and, correspondingly, cohesion improved. discussion could be efficiently formation which operated high conditions dynamic static loadings.