Metastable State in Aluminum-Silver Alloys Formed during Quenching
نویسندگان
چکیده
منابع مشابه
Metastable crystalline AuGe catalysts formed during isothermal germanium nanowire growth.
We observe the formation of metastable AuGe phases without quenching, during strictly isothermal nucleation and growth of Ge nanowires, using video-rate lattice-resolved environmental transmission electron microscopy. We explain the unexpected formation of these phases through a novel pathway involving changes in composition rather than temperature. The metastable catalyst has important implica...
متن کاملAluminum and Aluminum Alloys Casting Problems
Aluminum castings have played an integral role in the growth of the aluminum industry since its inception in the late 19th century. The first commercial aluminum products were castings, such as cooking utensils and decorative parts, which exploited the novelty and utility of the new metal. Those early applications rapidly expanded to address the requirements of a wide range of engineering speci...
متن کاملtransformation in metastable Fe - Mn alloys
Metastable Fe-Mn alloys exhibit a non-thermoelastic martensitic transformation which is accompanied by a significant thermal effect (ca. 20 J/g). Among Fe-Mn alloys, the highest value of latent heat was registered in alloys with 17-18 wt. % Mn. In this work we investigate effects of carbon (up to 0.4 wt. %) and cold rolling (5-25% of thickness reduction) on the latent heat and the temperature h...
متن کاملEvidence for Solute Drag during Recrystallization of Aluminum Alloys
Evidence of both solute drag as well as differences in migration mechanisms of certain boundary types has been found for an Al-Zr alloy. In-situ Transmission Electron Microscopy (TEM) annealing experiments coupled with Scanning Transmission Electron Microscopy (STEM) showed a stark contrast between Zr segregation at small and large scales. Specifically, Zr was found to segregate to, as well as ...
متن کاملLiquation Cracking of Dissimilar Aluminum Alloys during Friction Stir Welding
A liquation cracking mechanism of dissimilar Al alloys during the friction stir welding (FSW) is suggested in this study. To identify the mechanism, the precipitates were analyzed and Al-Mg-Cu phase diagrams were calculated. Electron backscattering diffraction (EBSD) analysis and electron probe microanalysis (EPMA) were also conducted. In the same manner as constitutional liquation, at high hea...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Japan Institute of Metals
سال: 1969
ISSN: 0021-4434,2432-4701
DOI: 10.2320/matertrans1960.10.132