Mesoporous Carbon Membranes with Controlled Pore Diameters
نویسندگان
چکیده
منابع مشابه
Fabrication and Characterization of Single Phase α-Alumina Membranes with Tunable Pore Diameters
Nanoporous and single phase α-alumina membranes with pore diameters tunable over a wide range of approximately 60-350 nm were successfully fabricated by optimizing the conditions for anodizing, subsequent detachment, and heat treatment. The pore diameter increased and the cell diameter shrunk upon crystallization to α-alumina by approximately 20% and 3%, respectively, in accordance with the 23%...
متن کاملPREPARATION OF NANO PORE MORDENITE MEMBRANES
Abstract: Nano pore Mordenite membranes were prepared on the outer surface of ceramic tubular tubes via hydrothermal synthesis and evaluated for dehydration pervaporation of water unsymmetrical dimethylhydrazine UDMH mixtures. Highly water-selective mordenite membranes were prepared and the optimum reaction condition was found to be 24 h crystallization time and 170 °C crystallization temperatu...
متن کاملTemplate Synthesis of Three-Dimensional Cubic Ordered Mesoporous Carbon With Tunable Pore Sizes
Three-dimensional cubic ordered mesoporous carbons with tunable pore sizes have been synthesized by using cubic Ia3d mesoporous KIT-6 silica as the hard template and boric acid as the pore expanding agent. The prepared ordered mesoporous carbons were characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption-desorption anal...
متن کاملSynthesis of mesoporous carbon nanoparticles with large and tunable pore sizes.
Mesoporous carbon nanoparticles (MCNs) with large and adjustable pores have been synthesized by using poly(ethylene oxide)-b-polystyrene (PEO-b-PS) as a template and resorcinol-formaldehyde (RF) as a carbon precursor. The resulting MCNs possess small diameters (100-126 nm) and high BET surface areas (up to 646 m(2) g(-1)). By using home-designed block copolymers, the pore size of MCNs can be tu...
متن کاملNano-porous anodic aluminium oxide membranes with 6–19 nm pore diameters formed by a low-potential anodizing process
Self-organized nano-porous anodic aluminium oxide (AAO) membranes with small pore diameters were obtained by applying a low anodizing potential in sulfuric acid solutions. The pore diameters of the as-prepared AAO membranes were in the range of about 6–19 nm and the interpore distances were about 20–58 nm. Low potentials (6–18 V) were applied in anodizing processes to make such small pores. A l...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MEMBRANE
سال: 2007
ISSN: 0385-1036,1884-6440
DOI: 10.5360/membrane.32.325