Mesoporous and Macroporous Alumina-Supported Nickel Adsorbents for Adsorptive Desulphurization of Commercial Diesel
نویسندگان
چکیده
منابع مشابه
Effect of Nickel Particle Size on Alumina Supported Nickel Catalysts for p-Nitrophenol Hydrogenation
The catalytic hydrogenation of p-nitrophenol to p-aminophenol was investigated over alumina supported nickel catalysts prepared by impregnation reduction method and mechanical mixing method. The catalysts were characterized by XRD and FESEM. The results show that the nickel particle diameter of alumina supported nickel prepared by impregnation reduction method (denoted as Ni/Al2O3) is slightly ...
متن کاملA facile route to ordered mesoporous-alumina-supported catalysts, and their catalytic activities for CO oxidation.
Well-dispersed noble metal nanoparticles can be synthesized, and further stabilized under high treatment temperature, by the confinement effect of ordered mesoporous alumina.
متن کاملSilane removal at ambient temperature by using alumina-supported metal oxide adsorbents.
Copper, zinc, and cerium oxide adsorbents supported on alumina were used to remove silane gas (SiH4). The adsorbents were prepared using a coprecipitation method and characterized by the inductively coupled plasma mass spectrometry, X-ray powder diffractometer, and Brunauer-Emmett-Teller method (BET). The silane removal efficiency and adsorption capacity of the adsorbents were investigated in t...
متن کاملMultiphase Assembly of Mesoporous-Macroporous Membranes
The synthesis of inorganic-organic composites and mesoporous materials with structures and functions over different length scales has ramifications in diverse areas, such as large-molecule catalysis, biomolecule separations, miniaturization of electronic devices, chromatographic supports, the formation of semiconductor nanostructures, and the development of medical implants.1-8 The use of organ...
متن کاملCatalytic Behavior of Chromium Oxide Supported on Nanocasting-Prepared Mesoporous Alumina in Dehydrogenation of Propane
Mesoporous alumina with narrow pore size distribution centered in the range of 4.4-5.0 nm and with a specific surface area as high as 270 m²·g-1 was prepared via the nanocasting approach using a CMK-3 carbon replica as a hard template. Based on this support, a series of catalysts containing 1, 5, 10, 20 and 30 wt % of chromium was prepared by incipient wetness impregnation, characterized, and s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید